3D Printing of Polyvinyl Alcohol Hydrogels Enabled by Aqueous Two-Phase System

Rahul Karyappa,Nidhi Nagaraju,Kento Yamagishi,Xue Qi Koh,Qiang Zhu,Michinao Hashimoto

DOI: https://doi.org/10.1039/d3mh01714a

IF: 13.3

2024-02-15

Materials Horizons

Abstract:The synthesis of PVA hydrogels (PVA-Hy) requires a high-concentration alkali solution (e.g., sodium hydroxide, NaOH, 14% w/w, 4.2 M), and the rapid physical crosslinking of PVA makes it challenging to ensure layer-to-layer adhesion for 3D printing. This work demonstrated the three-dimensional (3D) printing of PVA hydrogels in benign conditions (NaOH, 1% w/w, 0.3 M) using a two-phase system (ATPS). Salting out of PVA to form ATPS allowed temporal stabilization of 3D-printed PVA structures while it was physically crosslinked by moderate alkaline conditions. Crucially, the layer-to-layer adhesion of PVA was facilitated by delayed crosslinking of PVA at low alkaline concentrations that required additional reaction time. To verify this principle, we studied the feasibility of direct ink write (DIW) 3D printing of PVA inks (5 – 25% w/w, μ = 0.1 – 20 Pa·s, and MW = 22000 and 74800) in aqueous embedding media offering three distinct chemical environments: (1) salts for salting out (e.g., Na 2 SO 4 ), (2) alkali hydroxides for physical crosslinking (e.g., NaOH), and (3) mixture of salt and alkali hydroxide. Our study suggested the feasibility to 3D-print PVA-Hy using the mixture of salt and alkali hydroxide, demonstrating a unique concept of embedded 3D printing enabled by ATPS for temporary stabilization of the printed structures to facilitate 3D fabrication.

materials science, multidisciplinary,chemistry