High-load Mg2Ni nanoparticle-carbon nanofiber composites for hydrogen storage
Eduardo David Ruiz-Santacruz,José de Jesús Vega-Soria,Aura Karina Cruz-Jiménez,Uriel Caudillo-Flores,Nidia Libia Torres-García,Karina Suárez-Alcántara
DOI: https://doi.org/10.1039/d4nr01725k
IF: 6.7
2024-09-11
Nanoscale
Abstract:Herein, a simple synthesis method for Mg 2 Ni composites with carbon nanofibers capable of hydrogen storage is presented. Specifically, n -butyl- sec -butyl-magnesium solution in hexane (C 8 H 18 Mg, 0.7 M) and bis-cyclopentadienyl nickel( II ) (nickelocene or NiCp 2 ) were used as precursors for the Mg 2 Ni nanoparticles. Subsequently, the nanoparticles were composited with carbon nanofibers (CNF) with high loading of Mg 2 Ni of 50 wt%, 75 wt%, 90 wt%, and 100 wt%. The physicochemical characterization of the materials indicated that the size of the as-prepared Mg 2 Ni nanoparticles was less than 5 nm and they were highly agglomerated due to a carbon-based binder. The best hydrogen storage values were determined to be 2.6–2.7 wt%. Among the tested materials, the composite with 75 wt% of Mg 2 Ni in CNF presented the best hydrogen uptake. The pressure–composition–temperature curves indicated changes in the hydriding equilibrium pressures of the Mg 2 Ni nanoparticles compared to the material with a similar composition produced using ball-milling and thermodynamic calculations. Thus, the results presented herein indicate the beneficial effect of nanosizing on hydriding reactions.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry