Insight into SO2 poisoning over Cu-SAPO-18 used for NH3-SCR

Shujun Ming,Lei Pang,Zhen Chen,Yanbing Guo,Lei Guo,Qian Liu,Peng Liu,Yahao Dong,Shoute Zhang,Tao Li

DOI: https://doi.org/10.1016/j.micromeso.2020.110294

IF: 5.876

2020-08-01

Microporous and Mesoporous Materials

Abstract:The impact of SO2 poisoning on Cu-SAPO-18 physicochemical properties and its NH3-SCR reaction mechanism was investigated. After exposing Cu-SAPO-18 to SO2+O2 for 40 min, the sulfite and sulfate species were detected on Cu-SAPO-18 surface, which caused a small decrease in BET surface area and micropore volume, the increase in NH3 storage and the deactivation of some isolated Cu2+ sites. These could be interpreted by the slight micropore blocking, interaction between sulfates and NH3 forming new NH4 + species and the formation of Cu-sulfate, respectively. Additionally, it was observed that isolated Cu2+ ions in pear-shaped cavity of AEI structure, which are beneficial to good low-temperature deNOx activity, were more severely poisoned by SO2 than Cu2+ in the double 6-membered ring (D6R). Accordingly, the NH3-SCR activity below 350 °C was restrained by SO2. Moreover, the in-situ DRIFTS results indicate that Cu-SAPO-18 catalyzed NH3-SCR reaction predominantly proceeds through Langmuir−Hinshelwood (L−H) mechanism at low temperature. SO2 poisoning inhibited the adsorption of NO + O2 and NH3 on Cu2+ sites, thereby decreasing the formation of Cu−NOx and Cu−NH3 intermediates, evidently, the L−H mechanism was suppressed by SO2. Interestingly, the deactivated Cu-SAPO-18 could be regenerated under SCR gas at 550 °C and resumed at least most NH3-SCR activity.

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied