Electronic structure and thermal properties of Sm 3+ ‐doped La 2 Zr 2 O 7 : First‐principles calculations and experimental study
Yiming Li,Xuanyu Meng,Qian Chen,Jiatong Zhu,Jie Xu,Michael J. Reece,Feng Gao
DOI: https://doi.org/10.1111/jace.17561
IF: 4.186
2020-11-22
Journal of the American Ceramic Society
Abstract:<p>By applying the first‐principles calculation, the electronic structure, mechanical and thermal properties of Sm<sup>3+</sup>‐doped La<sub>2</sub>Zr<sub>2</sub>O<sub>7</sub> were investigated, and experiments were carried out to verify the theoretical results. As the Sm<sup>3+</sup> doping rate increases, the lattice parameters decrease while the theoretical density increases. The doping of Sm<sup>3+</sup> promotes the transformation from pyrochlore structure to defective fluorite structure. The Young's modulus of pure La<sub>2</sub>Zr<sub>2</sub>O<sub>7</sub> shows obvious anisotropy, while it tends to be isotropy with the doping of Sm<sup>3+</sup>. The calculated theoretical hardness is positively correlated with the doping rate, yet due to the solid solution strengthening effect, the materials with doping rate of 50% get the highest hardness. Based on the calculations and experiments, the optimal Sm<sup>3+</sup> doping rate of La<sub>2</sub>Zr<sub>2</sub>O<sub>7</sub> is 50%. LaSmZr<sub>2</sub>O<sub>7</sub> has hardness of 11.35GPa, the thermal conductivity of 1.35W/(m·K) at 1173K, and the thermal expansion coefficient of 10.12×10<sup>‐6</sup>/K at 1173K. The above results indicate that LaSmZr<sub>2</sub>O<sub>7</sub> has good mechanical and thermal properties, which provides new ideas for the selection of thermal barrier coating materials.</p>
materials science, ceramics