Shallow Iodine Defects Accelerate the Degradation of α-Phase Formamidinium Perovskite

Shaun Tan,Ilhan Yavuz,Marc H. Weber,Tianyi Huang,Chung-Hao Chen,Rui Wang,Hao-Cheng Wang,Jeong Hoon Ko,Selbi Nuryyeva,Jingjing Xue,Yepin Zhao,Kung-Hwa Wei,Jin-Wook Lee,Yang Yang

DOI: https://doi.org/10.1016/j.joule.2020.08.016

IF: 46.048

2020-11-01

Joule

Abstract:Shallow defects are mostly benign in covalent semiconductors, such as silicon, given that they do not constitute non-radiative recombination sites. In contrast, the existence of shallow defects in ionic perovskite crystals might have significant repercussions on the long-term stability of perovskite solar cells (PSCs) because of the metastability of the ubiquitous formamidinium lead triiodide (FAPbI ₃) perovskite and the migration of charged point defects. Here, we show that shallow iodine interstitial defects ( <math>Ii</math>) can be generated unintentionally during commonly used post-fabrication treatments, which can lower the cubic-to-hexagonal transformation barrier of FAPbI ₃-based perovskites to accelerate its phase degradation. We demonstrate that concurrently avoiding the generation of <math>Ii</math> and the more effective passivation of iodine vacancies ( <math>VI</math>) can improve the thermodynamic stability of the films and operational stability of the PSCs. Our most stable PSC retained 92.1 % of its initial performance after nearly 1,000 h of continuous illumination operational stability testing.

materials science, multidisciplinary,chemistry, physical,energy & fuels