N-doped magnetic three-dimensional carbon microspheres@TiO2 with a porous architecture for enhanced degradation of tetracycline and methyl orange via adsorption/photocatalysis synergy
Yushun Zhou,Taimei Cai,Shuai Liu,Yanyan Liu,Huijie Chen,Zhongtian Li,Jun Du,Zhiqiang Lei,Hailong Peng
DOI: https://doi.org/10.1016/j.cej.2021.128615
IF: 15.1
2021-05-01
Chemical Engineering Journal
Abstract:<p>Organic contaminants in aquatic ecosystems have raised serious environmental concerns and pose severe risks to human health, and the catalytic efficiency of traditional TiO<sub>2</sub> catalysts has been greatly limited by photogenerated electron/hole recombination. Therefore, a novel catalyst of N-doped magnetic three-dimensional (3D) carbon <sub>2</sub> with a nanofibrous porous architecture (N-doped <sub>2</sub>) was developed from the low-cost biomass of chitin. The N-doped <sub>2</sub> consist of N-doped carbon nanofibers, a 3D porous architecture, and a high surface area. TiO<sub>2</sub> nanoparticles were uniformly immobilized on the N-doped carbon nanofibers, resulting in many catalytic sites. The current density of N-doped <sub>2</sub> was approximately 0.247 uAcm<sup>−2</sup> with 1.65 times than that of pure TiO<sub>2</sub>, and the bandgap of N-doped <sub>2</sub> was only 1.91 eV. Additionally, N-doped <sub>2</sub> had excellent adsorption capability for tetracycline (TC) (60.38%) and methyl orange (MO) (40.15%) in the dark after 40 min. Under the optimized conditions, N-doped <sub>2</sub> exhibited remarkable photodegradation performance for MO and TC mixture solutions, the degradation efficiencies of MO and TC were approximately 83.80% and 74.37% under UV irradiation, and that of was maintained at 68.07% and 76.55% even in cloudy weather, respectively. Meanwhile, N-doped <sub>2</sub> possess good potential for practical applications with long-term stability and can be easily recycled from solutions under an external magnet. Therefore, this work provides new insight into the fabrication of low-cost biomass-based 3D hierarchical porous carbon materials and that can be used as high-performance photocatalysts for the degradation of organic contaminants.</p>
engineering, chemical, environmental