Strengthening by customizing microstructural complexity in nitrogen interstitial CoCrFeMnNi high-entropy alloys
Jing Zhang,Kook Noh Yoon,Min Seok Kim,Hea Sang Ahn,Ji Young Kim,Zehao Li,Taisuke Sasaki,Kazuhiro Hono,Eun Soo Park
DOI: https://doi.org/10.1016/j.jallcom.2021.163483
IF: 6.2
2022-04-01
Journal of Alloys and Compounds
Abstract:Interstitial alloying has been proved to be a promising option to improve the mechanical properties in various commercial alloys. Herein, we systematically investigate the microstructure evolution and mechanical property change of CoCrFeMnNi high-entropy alloys (HEAs) with varied nitrogen contents as an interstitial alloying element. To equilibrate the thermal history, all the alloys are heat-treated as follows: homogenization (1100 ℃ for 20 h), cold-rolling (reduction ratio of 60%), and subsequent annealing (900 ℃ for 3 min). In N1 alloy (CoCrFeMnNi HEA with 1 at% of nitrogen doping), we could observe fully recrystallized grains with a small amount of Cr2N precipitates. As the nitrogen contents increased to 3 at% (N3 alloy), the recrystallization was significantly retarded by the formation of 3 different types of Cr2N precipitates, leading to having ~60% of non-recrystallized grains. Furthermore, the various precipitates let the alloy have a heterogeneous complex microstructure. With increasing nitrogen contents, the yield strength and ultimate tensile strength can be improved without significant reduction of ductility, which exceeds those of Cantor HEA by nearly a factor of two. The effect of each strengthening mechanism on the improved strength in heterogeneous complex microstructure is systematically discussed. These results are expected to provide a novel guideline on how to effectively control key properties of HEAs by interstitial alloying through tailoring of heterogeneous microstructure as well as the inherent complexity of HEAs.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering