Abstract:A critical issue to tackle before successful commercialization of solid oxide fuel cells (SOFCs) can be achieved is the long-term thermal stability required for SOFCs to operate reliably without significant performance degradation despite enduring thermal cycling. In this work, the impact of thermal cycling on the durability of NiO-yttria-stabilized zirconia-based anode-supported cells is studied using three different heating/cooling rates (1, 2, and 5 °C min-1) as the temperature fluctuated between 400 and 700 °C. Our experiments simulate time periods when power from SOFCs is not required (e.g., as might occur at night or during an emergency shutdown). The decay ratios of the cell voltages are 8.8% (82 μV h-1) and 19.1% (187 μV h-1) after thermal cycling testing at heating/cooling rates of 1 and 5 °C min-1, respectively, over a period of 1000 h. The results indicate SOFCs that undergo rapid thermal cycling experience much greater performance degradation than cells that experience slow heating/cooling rates. The changes in total resistance for thermally cycled cells are determined by measuring the Rpol of the electrodes (whereas the ohmic resistances of the cells remain unchanged from their initial value), signifying that electrode deterioration is the main degradation mechanism for SOFCs under thermal cycling. In particular, fast thermal cycling leads to severe degradation in the anode part of SOFCs with substantial agglomeration and depletion of Ni particles seen in our characterizations with field emission-scanning electron microscopy and electron probe microanalysis. In addition, the mean particle size in the cathode after thermal cycling testing increases from 0.104 to 0.201 μm for the 5 °C min-1 cell. Further, the presence of Sr-enriched regions is more significant in the La0.6Sr0.4Co0.2Fe0.8O3-δ cathode after fast thermally cycled SOFCs.

Assessing performance degradation induced by thermal cycling in solid oxide cells

Solid Oxide Electrolysis Cell under Real Fluctuating Power Supply with a Focus on Thermal Stress Analysis

Thermal Management of Reversible Solid Oxide Cells in the Dynamic Mode Switching

Degradation Mechanisms of Solid Oxide Fuel Cells under Various Thermal Cycling Conditions

A Durability Model for Solid Oxide Fuel Cell Electrodes in Thermal Cycle Processes

Long-term thermo-mechanical performance evolution of a 15-cell solid oxide fuel cell stack

Performance Evolution Analysis of a Solid Oxide Cell Operated in Fuel-Cell, Electrolysis and Cycle Modes

Performance Degradation Analysis of Solid Oxide Fuel Cells Using Dynamic Electrochemical Impedance Spectroscopy

Quantifying the performance evolution of solid oxide fuel cells during initial aging process

Effect of Inhomogeneous Oxidation on the Mechanical Degradation of Anode Supported Solid Oxide Fuel Cell

Analysis of Electrochemical Degradation Phenomena of SOC Stacks Operated in Reversible SOFC/SOEC Cycling Mode

Thermal Stress Analysis at the Interface of Cathode and Electrolyte in Solid Oxide Fuel Cells

Long-term performance prediction of solid oxide electrolysis cell (SOEC) for CO2/H2O co-electrolysis considering structural degradation through modelling and simulation

Thermo-Electro-Chemo-Mechanical Modeling of Solid Oxide Fuel Cell for Stress and Failure Evolution During Duty Cycle

Degradation Analysis of Plasma Sprayed Metal-Supported Solid Oxide Fuel Cell: the Evolution of Electrode Processes under Polarization

A 3D Simulation of DC-Biased Electrochemical Impedance of Solid Oxide Electrolysis Cell: Effects of Delamination

A continuum modeling study on the electrochemical performance and stability of solid oxide cells and oxygen permeation membranes

Evolution of Thermal Stress and Failure Probability During Reduction and Re Oxidation of Solid Oxide Fuel Cell

A Model for the Delamination Kinetics of La0.8Sr0.2MnO3 Oxygen Electrodes of Solid Oxide Electrolysis Cells

Addressing planar solid oxide cell degradation mechanisms: A critical review of selected components