Microstructural development during crystallization firing of a dental-grade nanostructured lithia-zirconia glass-ceramic

Angel L. Ortiz,Camila S. Rodrigues,Fernando Guiberteau,Yu Zhang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.04.036
IF: 5.7
2021-09-01
Journal of the European Ceramic Society
Abstract:<p>The microstructural development during crystallization firing of a commercially-available dental-grade nanostructured lithia-zirconia glass-ceramic (Vita Suprinity® PC) was unraveled using a wide battery of <em>ex-situ</em> and <em>in-situ</em> characterization techniques. It was found that the milling blocks are slightly crystallized glass-ceramics, with a complex chemical composition and consisting of partially de-polymerized glass plus Li<sub>2</sub>SiO<sub>3</sub> nanocrystals. It was also found that during crystallization firing the glassy matrix first reacts with part of the Li<sub>2</sub>SiO<sub>3</sub> to form Li<sub>2</sub>Si<sub>2</sub>O<sub>5</sub> at ∼810-820 °C, and then Li<sub>3</sub>PO<sub>4</sub> precipitates from the glass. This results in glass-ceramics with abundant nanocrystals embedded in a sparse zirconosilicate glass matrix (containing many other cations subsumed) that, due to its high viscosity, inhibited crystal growth. Therefore, these dental glass-ceramics are not reinforced with ZrO<sub>2</sub> crystals unless over-fired above ∼890 °C and at the expense of its singular nanostructure. Finally, this study opens doors for optimizing the clinical performance of these dental glass-ceramics via microstructural tailoring.</p>
materials science, ceramics
What problem does this paper attempt to address?