Analysis Of Anti-Reflective And Self-Cleaning Coatings On Glass Substrates For Solar Panels

Arvind Kumar Singh,Sandeep Singh Kharb,Anup Malik

DOI: https://doi.org/10.1142/s0218625x2440002x

2024-10-18

Surface Review and Letters

Abstract:Surface Review and Letters, Ahead of Print. Dust and other environmentally suspended particles deposited on the solar panels reduce the sunlight to photovoltaic cells, reducing the total energy outcome. A dust-reflecting coating keeps a cleaner surface, thus enhancing light absorption and improving the overall energy outcome. This study synthesized the sol–gel of SiO2, MgF2, and TiO2 and made the coating on the glass substrate by SiO[math], SiO[math], and MgF[math] using sol–gel dip coating and spin coating method. Coatings that occurred on the glass sample surfaces were identified by using FTIR analysis. Five of the above six coatings made using different mixtures have increased transmittance than pure glass, while one SiO[math] spin coating reduced the transmittance. The minimum water contact angle of 37.69∘ was found on the SiO[math] spin-coated surface, and the maximum contact angle was 72.10∘ on the MgF2 dip-coated surface. This shows that the self-cleaning properties in SiO[math] spin-coated surfaces are maximum and minimum in MgF2 dip-coated surfaces. The angle found by the test shows that spin coating is a better technique than dip coating for hydrophilic surface coating. This was due to the more homogenous coating on the spin-coated sample surfaces. There was less accumulation of dust found on the coated surfaces compared to non-coated glass sample surfaces.

chemistry, physical,physics, condensed matter