Control over Phase Structures’ Evolution Within the Novel Organic–inorganic Hybrid System for Achieving a Comprehensive Thermal, Mechanical, and Dielectric Properties
Zichun Ding,Runze Liu,Yuhang Wang,Qing Wang,Jianjian Jiao,Jianing Guo,Jingyi Wang,Lishuai Zong,Xigao Jian,Jinyan Wang
DOI: https://doi.org/10.1016/j.cej.2024.155182
IF: 15.1
2024-01-01
Chemical Engineering Journal
Abstract:Significant challenges persist in developing high-performance, wave-transparent capable of operating above 500 degree celsius using organic-inorganic hybrid materials. This study introduced a novel, highly reactive terminal carborane monomer, 4-(3-carborylphenyl) phthalonitrile (CB-Ph), to create a cross-linked network structure and inorganic phase. By integrating this with the conventional high-performance poly (phthalazine ether nitrate ketone) (PPENK), a novel organic-inorganic hybrid system was successfully constructed. Simultaneously, the modifications in the inorganic layer and phase structure of the material with increasing CB-Ph content were examined through nanoindentation and SEM analysis systems, establishing a structural foundation for optimizing the balance between thermal resistance, mechanical strength, and dielectric properties (balance of T-M-D). The thermal performance testing results indicates that the hybrid materials achieved high glass transition temperatures (T-g exceeding 500 degree celsius). This enhancement is attributable to the synergistic effects of cyanide side group micro-crosslinking and the phthalonitrile crosslinking network, which collectively restricted the movement of chain segments. The P-CB50 resin (PPENK+50 wt% CB-Ph), with its distinctive transition phase structure, boasts the most outstanding comprehensive performance. In terms of thermal stability, it not only features a T-g surpassing 500 degree celsius In terms of thermal stability, it not only has a T-g exceeding 500 degrees C, but also loses only 5 % weight at 599.3 degrees C in a nitrogen atmosphere (T-d5%-N-2 = 599.3 degrees C). Mechanical testing reveals that the flexural strength of the P-CB50 composite reaches an impressive 384.3 MPa, while the impact strength attains a significant 109.4 KJ/m(2). Even at temperatures as high as 500 degree celsius, the dielectric constant of the P-CB50 composite material remains below 4, underscoring its superior high temperature wave-transparent properties. These results have firmly established a correlation between the phase structure of the hybrid system and the comprehensive performance of T-M-D, thereby laying a solid foundation for the development of high-temperature resistant and wave-transparent materials with enhanced overall performance.