TiO 2 @C catalyzed hydrogen storage performance of Mg-Ni-Y alloy with LPSO and ternary eutectic structure

Wenjie Song,Wenhao Ma,Shuai He,Wei Chen,Jianghua Shen,Dalin Sun,Qiuming Wei,Xuebin Yu

DOI: https://doi.org/10.1016/j.jma.2023.04.002

IF: 11.813

2023-05-14

Journal of Magnesium and Alloys

Abstract:A designed Mg 88.7 Ni 6.3 Y 5 hydrogen storage alloy containing 14H type LPSO (long-period stacking ordered) and ternary eutectic structure was prepared by regulating the alloy composition and casting. The hydrogen storage performance of the alloy was improved by adding nano-flower-like TiO 2 @C catalyst. The decomposition of the LPSO structure during hydrogenation led to the formation of plenty of nanocrystals which provided abundant interphase boundaries and activation sites. The nanoscale TiO 2 @C catalyst was uniformly dispersed on the surface of alloy particles, and the "hydrogen overflow'' effect of TiO 2 @C accelerated the dissociation and diffusion of hydrogen on the surface of the alloy particles. As a result, the in-situ endogenous nanocrystals of the LPSO structure decomposition and the externally added flower-like TiO 2 @C catalyst uniformly dispersed on the surface of the nanoparticles played a synergistic catalytic role in improving the hydrogen storage performance of the Mg-based alloy. With the addition of the TiO 2 @C catalyst, the beginning hydrogen desorption temperature was reduced to 200 °C. Furthermore, the saturated hydrogen absorption capacity of the sample was 5.32 wt.%, and it reached 4.25 wt.% H 2 in 1 min at 200 °C and 30 bar.

metallurgy & metallurgical engineering