Abstract:Low carbon and low alloy steel pipes, prevalent in natural gas transmission systems due to their affordability, weldability, and strength, are confronted with significant challenges such as hydrogen embrittlement (HE) when transitioning towards hydrogen energy systems. This necessitates innovative predictive strategies to overcome these hurdles. Most existing research on HE has focused on a limited range of low carbon and low alloy steels under specific experimental conditions and has been constrained by the limitations of experimental facilities. To expand the research scope, our study incorporated seven machine learning (ML) techniques: Random Forest (RF), Decision Tree (DT), Extreme Gradient Boosting (XGBoost), Gradient Boosting (GB), Adaptive Boosting (AdaBoost), Categorical Boosting (CatBoost), and Artificial Neural Networking (ANN). The aim is to predict the HE in terms of the degradation of mechanical properties, specifically the reduction in area. Drawing from tensile test data obtained from 47 distinct low carbon and low alloy steels under pressurized hydrogen gas conditions, we constructed and evaluated a range of ML models, with the aim of identifying the most efficacious one for our study. Our results indicated that the CatBoost ML model offered the best prediction of the reduction in the area of these steels in a hydrogen environment. The CatBoost model provided a low Mean Absolute Error (MAE) of 7.32, Mean Square Error (MSE) of 83.78, Root Mean Square Error (RMSE) of 9.15, and a coefficient of determination (R 2 ) value of 77.62% for the training data and 72.50% for the testing data. Furthermore, the CatBoost model identified hydrogen gas pressure and the steel's ultimate tensile strength as the most influential parameters, contributing 47.4% and 19.2% respectively to the prediction of HE. This research provides valuable insights into the development of advanced materials and infrastructure for efficient hydrogen gas transportation, supporting the broader shift towards a hydrogen-based energy economy.

Inspection of hydrogen transport equipment: A data-driven approach to predict fatigue degradation

Effects of Crack Position on Fatigue Life of Large Seamless Storage Vessels Made of 4130X for Hydrogen Refueling Station

Embrittlement, degradation, and loss prevention of hydrogen pipelines

Design Fatigue Life Evaluation of High-Pressure Hydrogen Storage Vessels Based on Fracture Mechanics

Computational predictions of hydrogen-assisted fatigue crack growth

Modeling of necking area reduction of carbon steel in hydrogen environment using machine learning approach

Neural Network-Assisted Probabilistic Creep-Fatigue Assessment of Hydrogenation Reactor with Physics-Based Surrogate Model

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

Prediction of Ductile Damage in Composite Material Used in Type IV Hydrogen Tanks by Artificial Neural Network and Machine Learning with Finite Element Modeling Approach

The Fatigue Threshold Computation Of Steel In Hydrogen Environment By Shakedown Analysis

Inspection Data‐based Prediction on Fatigue Crack of Orthotropic Steel Deck Using Interpretable Machine Learning Method

A new data-driven probabilistic fatigue life prediction framework informed by experiments and multiscale simulation

Hydrogen Assisted Crack Growth Rate Model Derived by Physical-Guided Piecewise Symbol Regression

A defect-based physics-informed machine learning framework for fatigue finite life prediction in additive manufacturing

A Review of Fatigue Crack Growth for Pipeline Steels Exposed to Hydrogen

Research on Fatigue Crack Propagation Prediction for Marine Structures Based on Automated Machine Learning

Statistical Learning Prediction of Fatigue Crack Growth Via Path Slicing and Re-Weighting

Predicting Fatigue Crack Growth via Path Slicing and Re-Weighting

Random Load Pattern Recognition of Test Road Based on a Laser Direct Writing Carbon-Based Strain Sensor and a Deep Neural Network

Hydrogen-Accelerated Fatigue of API X60 Pipeline Steel and Its Weld