Abstract:We report on laser performances obtained in Q-switch mode operation from buried depressed-cladding waveguides of circular shape (100 μm diameter) that were inscribed in Nd:YAG and Nd:YVO₄ media by direct writing with a femtosecond laser beam. The Q-switch operation was realized with a Cr4+:YAG saturable absorber, aiming to obtain laser pulses of moderate (few μJ) energy at high (tens to hundreds kHz) repetition rate. An average power of 0.52 W at 1.06 μm consisting of a train of pulses of 7.79 μJ energy at 67 kHz repetition rate, was obtained from a waveguide realized in a 4.8 mm long, 1.1-at % Nd:YAG ceramics; the pulse peak power reached 1.95 kW. A similar waveguide that was inscribed in a 3.4 mm long, 1.0-at % Nd:YVO₄ crystal yielded laser pulses with 9.4 μJ energy at 83 kHz repetition rate (at 0.77 W average power) and 1.36 kW peak power. The laser performances obtained in continuous-wave operation were discussed for each waveguide used in the experiments. Thus, a continuous-wave output power of 1.45 W was obtained from the circular buried depressed-cladding waveguide inscribed in the 1.1-at %, 4.8 mm long Nd:YAG; the overall optical-to-optical efficiency, with respect to the absorbed pump power, was 0.21. The waveguide inscribed in the 1.0-at %, 3.4 mm long Nd:YVO₄ crystal yielded 1.85 W power at 0.26 overall optical efficiency. This work shows the possibility to build compact laser systems with average-to-high peak power pulses based on waveguides realized by a femtosecond (fs) laser beam direct writing technique and that are pumped by a fiber-coupled diode laser.

Femtosecond laser writing of the depressed cladding buried channel waveguides in ZnS crystal

Single scan femtosecond laser transverse writing of depressed cladding waveguides enabled by three-dimensional focal field engineering.

Femtosecond Laser Writing of Depressed Cladding Waveguide and Its Applications

Enhanced nonlinear effects in femtosecond laser-inscribed depressed cladding waveguides in sapphire crystals

Passive Q-Switching by Cr4+:YAG Saturable Absorber of Buried Depressed-Cladding Waveguides Obtained in Nd-Doped Media by Femtosecond Laser Beam Writing

3D Laser Writing of Low‐Loss Cross‐Section‐Variable Type‐I Optical Waveguide Passive/Active Integrated Devices in Single Crystals

Direct writing waveguides inside YAG crystal by femtosecond laser

Fabrication of Polarization-Independent Single-Mode Waveguides in Lithium Niobate Crystal with Femtosecond Laser Pulses

Buried Depressed-Cladding Waveguides Inscribed in Nd3+ and Yb3+ Doped CLNGG Laser Crystals by Picosecond-Laser Beam Writing

Depressed-Cladding 3-D Waveguide Arrays Fabricated With Femtosecond Laser Pulses

Femtosecond laser written low-loss multiscan waveguides in fused silica

Fabrication of single-mode hybrid crystal-glass waveguides by direct femtosecond laser writing and thermal annealing

Femtosecond Laser-Written Waveguides in a Bismuth Germanate Single Crystal

Direct-writing of cladding waveguide in PMNPT crystal by femtosecond laser micromachining

Tapered depressed-cladding waveguide lasers modulated by Ag nanoparticles embedded in SiO2

Fabrication of polarization-independent waveguides deeply buried in crystal using aberration-corrected femtosecond laser direct writing

Femtosecond Laser Written Depressed-Cladding Waveguide 2 × 2, 1 × 2 and 3 × 3 Directional Couplers in Tm3+:YAG Crystal

Fabrication of Polarization-Independent Waveguides Deeply Buried in Lithium Niobate Crystal Using Aberration-Corrected Femtosecond Laser Direct Writing

Direct Writing of Channel Optical Waveguides in Er 3+ -Doped Aluminosilicate Glass by Low Repetition Rate Femtosecond Laser

Femtosecond-laser-written Microstructured Waveguides in BK7 Glass

Femtosecond laser inscription of depressed cladding single-mode mid-infrared waveguides in sapphire