Abstract:NiCoCrAlTaY coating is widely used in high temperature oxidation resistance, gas erosion protection and gas path sealing of hot-end parts of aeroengines and gas turbines. In this study, NiCoCrAlTaY coatings were prepared on cobalt-based superalloy substrates by high pressure cold spray technology. The microstructure, mechanical property and tribological behaviors of the coatings before and after thermal exposure at 1050 °C were systemically studied. The results showed that NiCoCrAlTaY coatings with very dense structure could be obtained by high-pressure cold spraying with nitrogen as carrier gas. The coating remained completely intimate with the substrate without any cracking and spalling after thermal exposure at 1050 °C for 500 h. Due to elemental diffusion at high temperatures, the coating formed a four-layer structure, including alumina film on the surface, β-NiAl phase depletion layer near the surface, intermediate layer containing β-NiAl phase and β-NiAl phase depletion layer near the substrate. With the prolongation of thermal exposure at 1050 °C, the thicknesses of β-NiAl phase depletion layers both near the surface and the substrate increased. The thickness and content of the intermediate β-NiAl phase layer decreased gradually during thermal exposure. Besides, the average hardness values of the coating rapidly decreased by about 30 % after thermal exposure at 1050 °C for 5 h. In particular, the hardness of the β-NiAl phase depletion layer near the surface substrate was lower than that of the intermediate area containing β-NiAl phase. Due to the microstructure and hardness evolution, the wear resistance of the coating decreased significantly after thermal exposure. The friction coefficient of the coating increased from 0.2 to 0.5, and the volume wear rate of the thermally exposed coating was about 4.5 times higher than that of the as-sprayed coating. The results of this study provide guidance for design and application of high-performance MCrAlY coatings.

CrO2(OH)2 volatilization rate and oxidation behavior prediction of the NiCr coating in air-H2O environment at 650 °C

Long-term oxidation behavior for Ni-5Al coating in Air-H 2 O at 650 °C

Effect of Chromium and Water Vapor of Low Carbon Steel on Oxidation Behavior at 1050 °C

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Comparative Study on Oxidation Behavior of Fe-5wt% Cr Alloy in Various Mixed Atmospheres at 900–1 000 °C

Oxidation behavior at 1100 °C of NiCrAlY coatings deposited by various PVD techniques

Microstructure evolution and high temperature air oxidation behaviour of thick Cr coatings at 1200°C

Comparative Study On Oxidation Behavior Of Fe-5wt% Cr Alloy In Various Mixed Atmospheres At 900-1000 Degrees C

High temperature induced “glaze” layer formed in HVOF-sprayed NiCrWMoCuCBFe coating and its wear reduction mechanism

Anisothermal Oxidation of Micro-Crystalline Ni-20Cr-5Al Alloy Coating at 850-1280°C

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Non-isothermal Oxidation and Ignition Prediction of Ti-Cr Alloys

The high-temperature oxidation and mechanical properties of the Cr/Zr and CrN/Zr coating

Oxidation Behaviour of Microcrystalline Ni-Cr-Al Alloy Coatings at 900°C

Effect of Water Vapour on the Oxidation of Fe–13Cr–5Ni Martensitic Alloy at 973K

High Temperature Oxidation Behaviors of Al/Cr Composite Coating on Ti2AlNb Alloy

Investigation of Oxidation Resistance of Cr-Mo Alloy Surface-modification Coatings

Thermal-mechanical driven oxidation of NiCr-Cr3C2-BaF2/CaF2 composite coating at high temperature

Comparison between oxidation kinetics of HVOF sprayed WC–12Co and WC–10Co–4Cr coatings

Effect of high temperature exposure on microstructure, mechanical and tribological properties of cold sprayed NiCoCrAlTaY coatings

Corrosive wear behavior of HVOF-sprayed micro-nano-structured Cr3C2–NiCr cermet coatings under aqueous media