Formation mechanism of hump defects in high-speed laser wire additive manufacturing

Wenhao Huang,Haihui Zhong,Xiaoxu Li,Yazhou Jia,Shiqi Sun,Na Wu

DOI: https://doi.org/10.1016/j.optlastec.2024.112239

IF: 4.939

2024-12-11

Optics & Laser Technology

Abstract:During the high-speed laser wire additive manufacturing process, defects such as hump formation are very likely to occur. This study utilized high-speed cameras to observe the flow behavior of the molten pool in real-time during the high-speed laser wire deposition process. It analyzed the primary mechanisms of hump defect formation and examined the influence of process parameters such as laser power, wire feed speed, wire feed angle, and travel speed on the propensity for hump formation. Based on the physical phenomena involved in laser melting at high speeds, a mathematical model of thermal-force coupling in the molten pool at high speeds is established, and a numerical simulation study of the formation process of hump defects is carried out. In the model, different thermal physical parameters and thermal-force input conditions were preset to conduct a comparative analysis of the hump defect formation process during high-speed laser wire additive manufacturing. This revealed the formation mechanism of hump defects in the high-speed deposition process of aluminum alloy laser wire and guided feasible strategies to suppress hump defects in practical manufacturing processes.

optics,physics, applied