Effect of raw material composition on microstructures and properties of microporous MgO–Mg(Al, Fe) 2 O 4 refractory aggregates
Qianlin Chen,Wen Yan,Zhe Chen,Han Wu,Yawei Li
DOI: https://doi.org/10.1016/j.ceramint.2023.08.017
IF: 5.532
2023-09-06
Ceramics International
Abstract:Microporous MgO–Mg(Al, Fe) 2 O 4 refractory aggregates were prepared by the in-situ decomposition synthesis method using the magnesite, Al(OH) 3 and Fe 2 O 3 as raw materials. The effect of raw material composition (theoretical Mg(Al, Fe) 2 O 4 contents were 0–55 wt %) on their microstructure and strengths was investigated. When the theoretical Mg(Al, Fe) 2 O 4 contents were relatively low (0–5.5 wt %), the number of neck connections between the particles in the microporous MgO–Mg(Al, Fe) 2 O 4 refractory aggregates was small. As the theoretical Mg(Al, Fe) 2 O 4 contents increased to be 11–22 wt %, the number of neck connections increased and the compressive strengths were enhanced. When the theoretical Mg(Al, Fe) 2 O 4 contents increased to be excessive (33–55 wt %), the inter-particle pore size further increased due to the increase of volume expansion caused by the formation of more spinel, resulting in a decrease of compressive strength. Overall, when the theoretical Mg(Al, Fe) 2 O 4 contents were 11–22 wt %, the microporous MgO–Mg(Al, Fe) 2 O 4 refractory aggregates showed the excellent performances with the median pore sizes of 17.37–25.46 μm, the apparent porosities of 23.4–28.1%, the bulk densities of 2.57–2.79 g/cm 3 as well as the compressive strengths of 41.2–75.8 MPa.
materials science, ceramics