Enhancement of aqueous stability of NH2-MIL-101(Fe) by hydrophobic grafting post-synthetic modification

Jianwei Fu,Lin Wang,Yuheng Chen,Deyi Yan,Huase Ou
DOI: https://doi.org/10.1007/s11356-021-14834-1
IF: 5.8
2021-07-17
Environmental Science and Pollution Research
Abstract:The development of water-stable metal-organic frameworks is a critical issue for their photocatalysis applications in water treatment. A phenyl-ethyl side chain with low surface energy was grafted into NH2-MIL-101(Fe) through a post-synthetic modification (PSM) method. As a result, a novel MIL-101(Fe)-1-(4-(ethyl)phenyl)urea (named MIL-101(Fe)-EPU) was synthesized. Basic morphology, crystal structure, and chemical bond features of MIL-101(Fe)-EPU were retained after PSM. Nitrogen X-ray photoelectron spectroscopy analysis confirmed the successful introduction of the phenyl-ethyl side chain, and this transformation increased its hydrophobicity and water stability. Contact angles of MIL-101(Fe)-EPU to water raised from 59.6 to 140.4°. And its structure maintained intact after 72 h water exposure, indicating higher stability than parent NH2-MIL-101(Fe). In the photocatalysis reaction with visible light and oxidant donor (H2O2), MIL-101(Fe)-EPU demonstrated a degradation efficiency of tetrabromobisphenol A with a reaction rate at 0.0313 min−1. The predominant reaction mechanism was OH·oxidation. The acid condition was beneficial for this photocatalysis reaction and high stability was observed. Besides, photocatalysis efficiency, crystal structure, and chemical structures were all retained in different actual water mediums, suggesting high adaptability of MIL-101(Fe)-EPU. In general, hydrophobic group grafting using a PSM method endows MIL-101(Fe)-EPU the potentiality as photocatalyst for organic contaminant elimination from water.
environmental sciences
What problem does this paper attempt to address?
The paper primarily addresses the issue of insufficient stability of metal-organic framework materials (MOFs) in aqueous environments, particularly focusing on iron-containing MOFs (Fe-MOFs). Specifically, the study introduces low-surface-energy phenylethyl side chains on the surface of NH2-MIL-101(Fe) through a post-synthetic modification (PSM) method, thereby enhancing the material's hydrophobicity and water stability. The modified material is named MIL-101(Fe)-EPU. Experimental results show that the contact angle of MIL-101(Fe)-EPU in water increased from 59.6 degrees to 140.4 degrees, indicating a transition of its surface properties from hydrophilic to hydrophobic. Additionally, even after 72 hours of exposure in water, the structure of MIL-101(Fe)-EPU remained intact, demonstrating higher stability compared to the original NH2-MIL-101(Fe). Further research found that MIL-101(Fe)-EPU exhibited good photocatalytic degradation performance for tetrabromobisphenol A (TBBPA) in the presence of visible light and hydrogen peroxide (H2O2), with a reaction rate of 0.0313 min⁻¹. The main reaction mechanism is hydroxyl radical (OH·) oxidation, and acidic conditions favor the photocatalytic reaction. In summary, the introduction of hydrophobic groups through post-synthetic modification not only retains the inherent structure and function of the original MOF but also endows MIL-101(Fe)-EPU with better water stability and the ability to remove harmful organic pollutants from water as a photocatalyst.