Xiaolei Zhang,Qilu Yao,Haochong Wu,Yuanlan Zhou,Meihua Zhu,Zhang-Hui Lu
DOI: https://doi.org/10.1016/j.apcatb.2023.123153
2023-08-08
Abstract:Constructing efficient, durable, and economical catalysts to promote hydrogen production from hydrous hydrazine (N 2 H 4 ·H 2 O) is crucial, but still a great challenge. Herein, noble-metal-free Cr(OH) 3 -modified Ni nanoparticles (NPs) (2.7 nm) supported on defect-rich carbon-doped mesoporous TiO 2 nanosheets (C-TiO 2 ) were prepared for the first time via a simple and green wet-chemistry approach, in which the amount of oxygen defect in C-TiO 2 can be easily regulated by adjusting the amount of carbon doping. Significantly, the defect rich Ni-Cr(OH) 3 /C-TiO 2 catalyst presented 100% H 2 selectivity, ultrahigh catalytic activity, and remarkable durability for N 2 H 4 ·H 2 O dehydrogenation, with a turnover frequency (TOF) value of 266 h −1 at 323 K, more than 6-fold improvement than that of the Ni-Cr(OH) 3 /TiO 2 (41 h −1 ), which is among the highest values reported so far for noble-metal-free catalysts. The superior catalytic efficiency and durability are mainly owing to the small-sized and electron-rich of Ni NPs induced by the oxygen defects in C-TiO 2 , where the more oxygen defects, the better the catalytic activity. Furthermore, the catalyst also showed outstanding catalytic efficiency (TOF = 577 h −1 ) and robust durability for complete dehydrogenation of hydrazine borane (N 2 H 4 BH 3 ) at 323 K. This work provides inspiration for the construction of defect engineering and new insights for the development of low-cost and efficient heterogeneous hydrogen production catalysts.
chemistry, physical,engineering, chemical, environmental