Abstract:Atmospheric plasma sprayed (APS) thermal barrier coatings (TBCs) with lamellar structure exhibit low thermal conductivity and low stiffness. However, high temperature exposure for certain long duration causes the sintering which heals two-dimensional (2D) inter-lamellar pores and intrasplat pores. Such sintering effect increases the stiffness and thermal conductivity of the coatings and consequently reduces the stability and durability of TBCs. It can be expected that large 2D pores with a wide opening is difficult to be eliminated. In this study, inter-lamellar 2D pores with large opening width were fabricated in the La2Zr2O7 (LZO) coatings through spraying LZO+SrO coatings and removing the SrO splats in the water. Then, the conventional LZO coating and the porous LZO coating were subjected to high temperature exposure in the air at 1300 °C for different durations. The microstructure evolution especially in terms of the shape and density of inter-lamellar 2D pores was examined. In addition, the change of thermo-physic properties and the mechanical properties of the coatings with increasing exposure duration were studied. Results show that the 2D pores in LZO coating created by those SrO splats inherit primarily large opening width from 200nm to about 1 µm which endows the LZO coating with high sustainability at high temperature environment. Under thermal exposure at 1300oC, it was found that 2D pores resulting from SrO splats are free from healing while conventional 2D inter-lamellar pores with small opening width formed during splat cooling became healed rapidly. Thus, thermal conductivity and Young's modulus of the conventional LZO coating increased rapidly, while unhealed 2D pores in the highly porous LZO coatings contributed to the low Young's modulus and low thermal conductivity of LZO coating with remarkably high stability. With addition of 30% SrO in spray powder, a LZO coating with a thermal conductivity of about 0.39 W.m-1.K-1 in the as-prepared state was obtained. The coating maintained a thermal conductivity of 0.57 W.m-1.K-1 even after 100 hours exposure at 1300°C. The present results indicated that high sintering-resistant thermal barrier coating can be fabricated though designing inter-lamellar 2D pores with large opening width in the coating by the present novel approach.

Plasma sprayed K2Ti6O13 as thermal barrier coatings with high thermal swing for diesel piston enabled by inter-splat bonding and porosity tailoring

Thermo-Physical Properties of Plasma-Sprayed K2Ti6O13 Coatings for Diesel Engine Piston

Effect of spraying ceramic powder pore structure on thermophysical properties of plasma-sprayed thermal barrier coatings

Fabrication and characterization of thermal barrier coatings for internal combustion engines via suspension plasma spray with high solid loading

Plasma Spraying of Dense Ceramic Coating with Fully Bonded Lamellae Through Materials Design Based on the Critical Bonding Temperature Concept

Formation of high heat resistant coatings by using gas tunnel type plasma spraying

Wide-velocity Range High-Energy Plasma Sprayed Yttria-Stabilized Zirconia Thermal Barrier Coating — Part II: Structural Defects and Thermal-Bonding Properties

High Sintering-Resistant Plasma-Sprayed Thermal Barrier Coatings Designed with Large Two-Dimensional Inter-Lamellar Pores

Experimental investigation of the relationship between thermal barrier coating structured porosity and homogeneous charge compression ignition engine combustion

High Performance Nanostructured ZrO2 Based Thermal Barrier Coatings Deposited by High Efficiency Supersonic Plasma Spraying

High Heat Insulating Thermal Barrier Coating Designed with Large Two-Dimensional Inter-lamellar Pores

High Temperature Oxidation and Insulation Behavior of Plasma-Sprayed Nanostructured Thermal Barrier Coatings

Bimodal TBCs with low thermal conductivity deposited by a powder-suspension co-spray process

Cobalt- and Chromium-Oxide-Based Coatings: Thermally Spraying a Glaze Layer

Achieving high anti-sintering performance of plasma-sprayed YSZ thermal barrier coatings through pore structure design

Sintering Behavior of a Nanostructured Thermal Barrier Coating Deposited Using Electro‐sprayed Particles

Novel-structured plasma-sprayed thermal barrier coatings with low thermal conductivity, high sintering resistance and high durability

Enhanced thermal radiation blocking of plasma spraying thermal barrier coatings with a bimodal splat thickness distribution

Anodic plasma electrolytic deposition of composite coating on ferrous alloys with low thermal conductivity and high adhesion strength

Thermophysical properties and cyclic lifetime of plasma sprayed SrAl 12 O 19 for thermal barrier coating applications

Near Infrared Radiative Properties of Thermal Barrier Coatings