Preparation of Self-supporting Bagasse Cellulose Nanofibrils Hydrogels Induced by Zinc Ions

Peng Lu,Ren Liu,Xin Liu,Min Wu

DOI: https://doi.org/10.3390/nano8100800

2018-10-08

Abstract:Cellulose hydrogels are often prepared from native cellulose through a direct cellulose dissolution approach that often involves tedious process and solvent recovery problems. A self-supporting cellulose hydrogel was prepared by gelation of the TEMPO-oxidized bagasse cellulose nanofibrils (CNF) triggered by strong crosslinking between carboxylate groups and Zn2+. TEMPO process was used to generate negatively charged carboxylate groups on CNF surface to provide a high binding capability to Zn2+. Three TEMPO-oxidized CNFs of different carboxylate contents were prepared and characterized. TEM and AFM microscopes suggested that the sizes of CNFs were fined down and carboxylated cellulose nanofibrils (TOCNFs) of 5⁻10 nm wide, 200⁻500 nm long, and carboxylate contents 0.73⁻1.29 mmol/g were obtained. The final structures and compressive strength of hydrogels were primarily influenced by interfibril Zn2+-carboxylate interactions, following the order of TOCNFs concentration > content of carboxylate groups > concentration of zinc ions. A CO₂ sensitive self-supporting cellulose hydrogel was developed as a colorimetric indicator of food spoilage for intelligent food packaging applications.