Abstract:Macroporous materials polymerized from high internal phase emulsions (PolyHIPEs) possess well-defined interconnected porous structures and tunable device shapes. This provides interesting property characteristics well-suited for a variety of applications. However, such materials also demonstrate poor mechanical performances, which limit their potential use. As will be demonstrated, this results from the high surfactant content required by PolyHIPEs. Herein, a new approach is introduced for designing a highly efficient polymeric surfactant, which generates interconnected pores in PolyHIPEs through designing an incompatible surfactant and skeleton material. The surfactant also possesses a hyperbranched topology, which combines the strong amphipathy of small molecular surfactants and the nanosphere structure of Pickering emulsifiers to provide an excellent colloidal stability to HIPEs. A hyperbranched polyethylene having pendant sodium sulfonate groups (HBPE-SO3Na) was thus designed and synthesized via chain walking copolymerization of ethylene and 2-trimethylsilyloxyethyl acrylate followed by sulfonation. Stable HIPEs of styrene/divinylbenzene and water at a weight ratio of 1 to 5 were obtained with using HBPE-SO3Na. The polymerization of HIPEs produced interconnected macroporous polystyrenes (PSs) at a substantially lower surfactant content, for example, 0.5 wt % HBPE-SO3Na. The compressive Young's moduli of PolyHIPEs reached 104-111 MPa with 0.5-2 wt % HBPE-SO3Na, which is the first reported case of a PS-based PolyHIPE achieving its theoretical modulus. The PolyHIPE was used to support Au nanoparticles and embed in a column for oxidation of dimethylphenylsilane. A complete conversion of dimethylphenylsilanol was achieved with low column back pressure in a 50 h continuous reaction with no degradation of PolyHIPE integrity and mechanical property.

The aetiological relationship between herpes simplex virus type 2 and carcinoma of the cervix: an unanswered or unanswerable question?

Interconnected Porous Monolith Prepared Via UiO-66 Stabilized Pickering High Internal Phase Emulsion Template

MOF‐Based Hierarchically Porous Monoliths Prepared Via High Internal Phase Emulsion Template: Morphology, Thermal Stability, Mechanical Property, and MOF Accessibility

In-situ construction of hierarchically porous MOF monoliths using high internal phase emulsion templates

Structuring Metal-Organic Framework Materials into Hierarchically Porous Composites Through One-Pot Fabrication Strategy

Fabrication of Hydrophilic and Sponge-Like PVDF/brush-like Copolymer Blend Membranes Using Triethylphosphate As Solvent

Pickering medium internal phase emulsions based on natural clay particles: Route to a macroporous adsorbent

Miniemulsion Template Polymerization to Prepare a Sub-Micrometer Porous Polymeric Monolith with an Inter-Connected Structure and Very High Mechanical Strength

Porous Mullite Ceramics with Hierarchical Pores Constructed Via Vat Photopolymerization of Multi-Phase Pickering Emulsion

Toward Maximizing the Mechanical Property of Interconnected Macroporous Polystyrenes Made from High Internal Phase Emulsions.

Construction and Preparation Mechanism of Hierarchically Porous Sio2 Monoliths

Spontaneous Preparation Of Hierarchically Porous Silica Monoliths With Uniform Spherical Mesopores Confined In A Well-Defined Macroporous Framework

Hierarchically Porous Monolith with High MOF Accessibility and Strengthened Mechanical Properties using Water‐in‐Oil High Internal Phase Emulsion Template

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Preparation of Hierarchical Porous Monoliths With High Surface Areas by a Solvent Knitting Strategy

Interconnected Porous Polymers with Tunable Pore Throat Size Prepared Via Pickering High Internal Phase Emulsions

Macroporous Graphene Oxide-Polymer Composite Prepared Through Pickering High Internal Phase Emulsions

Interconnected Macroporous Polymers Synthesized from Silica Particle Stabilized High Internal Phase Emulsions

Pore Structure of Macroporous Polymers Using Polystyrene/Silica Composite Particles As Pickering Stabilizers.

CO2-Switchable Hierarchically Porous Zirconium-Based MOF-Stabilized Pickering Emulsions for Recyclable Efficient Interfacial Catalysis

Preparation of Carboxymethyl Cellulose-Based Macroporous Adsorbent by Eco-Friendly Pickering-MIPEs Template for Fast Removal of Pb2+ and Cd2+