Single-crystalline TiO2 Nanoparticles for Narrowing the Scalability Gap towards Stable and Efficient Perovskite Modules
Yong Ding,Bin Ding,Hiroyuki Kanda,Onovbaramwen Jennifer Usiobo,Thibaut Gallet,Zhenhai Yang,Yan Liu,Hao Huang,Jiang Sheng,Cheng Liu,Yi Yang,Valentin Queloz,Xianfu Zhang,Jean-Nicolas Audinot,Alex Redinger,Wei Dang,Edoardo Mosconi,Wen Luo,Filippo De Angelis,Mingkui Wang,Jihuai Wu,GuanJun Yang,Songyuan Dai,Paul Dyson,MOHAMMAD KHAJA Nazeeruddin
DOI: https://doi.org/10.21203/rs.3.rs-737440/v1
2021-01-01
Abstract:Abstract Remarkable progress in power conversion efficiency of perovskite solar cells (PSCs) has been achieved over the last decade, reaching 25.5%. However, transferring these accomplishments from individual small-size devices into large-area modules while preserving their commercial competitiveness compared to other thin-film solar cells remains a challenge. A major obstacle is to reduce the resistive losses and the number of intrinsic defects of electron transport layers (mesoporous TiO2, ETL) and to fabricate high-quality large-area perovskite films. Here, we report a facile solvothermal method to synthesize single-crystalline TiO2 rhombus-like nanoparticles with exposed {001} facets. Owing to their low lattice mismatch with the perovskite absorber, high electron mobility and lower density of defects, single-crystalline TiO2 nanoparticle-based small-size devices (0.09 cm2) achieve an efficiency of 24.05% and a fill factor of 84.7%. Importantly, these devices maintain about 90% of their initial performance after continuous operation for 1400 h. Combined with vacuum quenching-assisted techniques, we have fabricated large-area modules and obtained a certified efficiency of 22.72% with an active area of nearly 24 cm2. This represents the highest efficiency modules with the lowest efficiency loss between small-size devices and modules, enabling to reproducibly fabricate stable and efficient PSC modules.