Ultrahigh dielectric breakdown strength and excellent energy storage performance in lead-free barium titanate-based relaxor ferroelectric ceramics via a combined strategy of composition modification, viscous polymer processing, and liquid-phase sintering

Gang Liu,Yang Li,Biao Guo,Mingyang Tang,Quan Li,Jia Dong,Linjiang Yu,Kun Yu,Yan Yan,Dawei Wang,Leiyang Zhang,Haibo Zhang,Zhanbing He,Li Jin

DOI: https://doi.org/10.1016/j.cej.2020.125625

IF: 15.1

2020-10-01

Chemical Engineering Journal

Abstract:<p>BaTiO₃ (BT)-based lead-free ceramics are regarded as one kind of prospective candidates for next generation pulsed power capacitors due to their environmentally friendly and relatively high energy storage properties. Nevertheless, BT-based ceramics are still suffering from their small recoverable energy storage density (<em>W</em>_rec &lt; 3 J cm⁻³) and relatively low electric breakdown strength (BDS &lt; 350 kV cm⁻¹). Herein, we proposed a combined strategy via composition modification, viscous polymer processing, and liquid-phase sintering into BT-based ceramics to improve their BDS and <em>W</em>_rec. Both an ultrahigh BDS (&gt;410 kV cm⁻¹) and a large <em>W</em>_rec (3.54 J cm⁻³) are achieved in Sr_0.7Bi_0.2TiO₃ and Li₂CO₃ modified BT ceramic simultaneously. High <em>W</em>_rec (&gt;2.5 J cm⁻³ at 300 kV cm⁻¹) with small variation is maintained over a wide temperature range (30–150 °C) and frequency range (0.1–100 Hz), demonstrating very excellent temperature and frequency stability. The recorded ultrahigh BDS with high <em>W</em>_rec achieved in this work indicates that our combined strategy is effective to elevate the electric energy storage performances of BT-based dielectric ceramics and could be further generalized to other ceramic materials for the applications of advanced pulsed power capacitors.</p>

engineering, chemical, environmental