Self-reinforced and eco-friendly porous MgO-based ceramics from magnesite tailings: The effect of La2O3 and firing temperature

Xinming Ren,Beiyue Ma,Shuli Sun,Zhihui Wang,Wei Ji,Shengying Hou,Gaofeng Fu,Chengji Deng

DOI: https://doi.org/10.1016/j.ceramint.2024.01.209

IF: 5.532

2024-01-01

Ceramics International

Abstract:In the context of carbon peak and carbon neutrality, the resource utilization of solid waste tailings has important scientific research value and environmental protection significance. In this work, porous MgO-based ceramics with excellent mechanical and thermal insulation properties were prepared by the direct firing method and using lanthana as an additive. The results shows that the 2CaO·4La2O3·6SiO2 phase in-situ formed by the lanthana additive simultaneously improves the apparent porosity, thermal insulation, and mechanical properties of the prepared MgO-based ceramics. In particular, the 2CaO·4La2O3·6SiO2 phase increases apparent porosity by inhibiting shrinkage, from 51.78% to 53.34% (with 7.5 wt% of lanthana), and the thermal conductivity correspondingly decreases from 0.493 to 0.324 W·m−1 K−1 (800 °C); meanwhile, the 2CaO·4La2O3·6SiO2 phase improves the cold cpmpressive strength (from 6.89 to 11.13 MPa) and refractoriness under load (from 1345 to 1405 °C) by modifying the low-melting phase and cross-connecting the rod-like structure, respectively. Consequently, a potential strategy for the utilization of magnesite tailings is proposed, and the prepared porous ceramics are expected to be applied in the field of high-temperature thermal insulation.

materials science, ceramics