Investigation of the structural, morphological and magnetic properties of barium hexaferrite added with magnesium oxide nanoparticles
Majed Sharrouf,R. Awad,Khulud Habanjar
DOI: https://doi.org/10.1007/s00339-023-07079-x
2023-11-02
Applied Physics A: Materials Science and Processing
Abstract:(BaFe 12 O 19 ) 1 − x /(MgO) x nanocomposites, with weight fraction x = 0, 0.1, 0.2, 0.4, 0.8 and 1, have been synthesized by co-precipitation method followed by high-speed ball-milling techniques. Structural, optical, and magnetic properties have been studied. XRD analysis confirmed the formation of the two pure phases BaFe 12 O 19 and MgO, with the formation of a MgFe 2 O 4 as a minor phase in the nanocomposites. Transmission electron microscopy (TEM) followed by high resolution TEM and SAED were used to study the morphology, crystallinity and lattice spacing, respectively. TEM micrographs revealed the co-existence of spherical and nanorod-shaped particles for pure BaFe 12 O 19 , and cubic shape for MgO nanoparticles. Raman spectrum for BaFe 12 O 18 showed strong and sharp modes, identifying the formation of barium hexaferrite phase. However, MgO showed two broad peaks attributed to G and D bands. The energy dispersive X-ray and scanning electron microscope were performed for elemental analysis and surface topography, respectively. The real elemental compositions matched well with the starting values. X-ray photoelectron spectroscopy was conducted for the investigation of the elemental compositions and the oxidation states of (Ba 2+ , Fe 2+ , Fe 3+ Mg 2+ and O 2− ). The magnetic properties like saturation magnetization, remanent magnetization, coercivity and squareness ratio have been determined using the M – H loops. These loops revealed the hard ferromagnetic behavior of pure barium hexaferrite and the mixture of ferromagnetism with diamagnetic behavior at high fields for pure MgO. The saturation and remanent magnetizations decreased with the addition of MgO phase. d M /d H curves showed a weak magnetic coupling between the hard magnetic BaFe 12 O 19 and the soft magnetic MgFe 2 O 4 .