Dielectric relaxation and conduction behaviors of Aurivillius Na0.5Bi4.5Ti4O15 ceramics with Na doping

Fida Rehman,Jing-Bo Li,Pervaiz Ahmed,Muhammad Sheraz Khan,Yasir Saeed,Asma khan,Muhammad Zubair

DOI: https://doi.org/10.1007/s12598-020-01634-8

IF: 6.318

2021-01-09

Rare Metals

Abstract:<p class="a-plus-plus">Aurivillius Na<sub class="a-plus-plus">0.5</sub>Bi<sub class="a-plus-plus">4.5</sub>Ti<sub class="a-plus-plus">4</sub>O<sub class="a-plus-plus">15</sub> and Bi<sub class="a-plus-plus">4</sub>Ti<sub class="a-plus-plus">3</sub>O<sub class="a-plus-plus">12</sub> compounds were synthesized via solid-state reaction technique. X-ray powder diffraction study confirmed monophasic four-layered Na<sub class="a-plus-plus">0.5</sub>Bi<sub class="a-plus-plus">4.5</sub>Ti<sub class="a-plus-plus">4</sub>O<sub class="a-plus-plus">15</sub> and three-layered Bi<sub class="a-plus-plus">4</sub>Ti<sub class="a-plus-plus">3</sub>O<sub class="a-plus-plus">12</sub> ceramics. Dielectric relaxation and conduction behaviors of Na-contained Na<sub class="a-plus-plus">0.5</sub>Bi<sub class="a-plus-plus">4.5</sub>Ti<sub class="a-plus-plus">4</sub>O<sub class="a-plus-plus">15</sub> ceramics were thoroughly investigated in a large scale of temperature of 30–650 °C and frequency of 40 Hz–1 MHz. In addition, comparative studies of both the compounds were discussed. Impedance and modulus analyses revealed a single relaxation behavior in Na<sub class="a-plus-plus">0.5</sub>Bi<sub class="a-plus-plus">4.5</sub>Ti<sub class="a-plus-plus">4</sub>O<sub class="a-plus-plus">15</sub> compound which was originated from the grain's interior with grain resistance of 2.189 × 10<sup class="a-plus-plus">5</sup> Ω and capacitance of 4.268 × 10<sup class="a-plus-plus">−10</sup> F at 570 °C. While in Bi<sub class="a-plus-plus">4</sub>Ti<sub class="a-plus-plus">3</sub>O<sub class="a-plus-plus">12</sub> ceramic the relaxation was due to the contributions of grain and grain boundaries. Alternating current (AC) conductivity analysis revealed the presence of two different conduction regions in both the compounds. Activation energies for the two different conduction mechanisms, i.e., in low-temperature region and in high-temperature region were calculated to be ~ 0.23 and ~ 1.27 eV at 1 kHz for Na<sub class="a-plus-plus">0.5</sub>Bi<sub class="a-plus-plus">4.5</sub>Ti<sub class="a-plus-plus">4</sub>O<sub class="a-plus-plus">15</sub> compound and ~ 0.43 eV and ~ 0.97 eV at 1 kHz for Bi<sub class="a-plus-plus">4</sub>Ti<sub class="a-plus-plus">3</sub>O<sub class="a-plus-plus">12</sub> compound, respectively. The present study of dielectric relaxation and conduction behaviors would be helpful for further investigations of Na<sub class="a-plus-plus">0.5</sub>Bi<sub class="a-plus-plus">4.5</sub>Ti<sub class="a-plus-plus">4</sub>O<sub class="a-plus-plus">15</sub>-related Aurivillius compounds.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering