Achieving high energy density and long cycle life of high-voltage cathode LiNi 0.5 Mn 1.5 O 4 for lithium metal batteries: Suppressing the phase transition from cubic phase to tetragonal phase via Ta doping

Zhen Zhang,Chengkang Chang

DOI: https://doi.org/10.1016/j.ceramint.2023.10.309

IF: 5.532

2023-12-07

Ceramics International

Abstract:LiNi 0.5 Mn 1.5 O 4 has been disregarded in the electric vehicle battery market due to its low capacity. Extending the voltage range to 2 V–5 V enables excess Li + insertion into the 16c octahedral sites of the spinel lattice, leading to a substantial improvement in specific capacity and energy density. The surplus of Li + can be appropriately supplied by the metallic lithium at the anode of lithium metal batteries (LMBs). Nevertheless, severe capacity decay is still a problem. To solve this problem, Ta-doped LiNi 0.5 Mn 1.5 O 4 materials with excellent performance were achieved in this study. The resulting LiNi 0.5 Mn 1.485 Ta 0.015 O 4 sample exhibits the best electrochemical performance with an initial capacity of 233 mAh g −1 at 0.1 C, an energy density of 825 Wh kg −1 , and a capacity retention of 81.6 % after 100 cycles at 1C. Such promoted electrochemical performance is primarily attributed to the strong Ta–O bond energy (805 kJ mol −1 ), which inhibits the phase transition from cubic to tetragonal phase at the 2.7 V plateau, minimizes the volume changes and stabilizes the crystal structure. Furthermore, Ta doping stabilizes the three-dimensional channel for diffusion of Li + ions, which leads to enhanced rate capability (from 123 mAh g −1 to 161.5 mAh g −1 at 2 C).

materials science, ceramics