Abstract:The high-temperature composite phase change materials (HCPCMs) were prepared from solid waste blast furnace slag (BFS) and NaCl-KCl binary eutectic salt to achieve efficient and cost-effective utilization. To ensure good chemical compatibility with chlorine salt, modifier fly ash (FA) was incorporated and subjected to high-temperature treatment for the processing of industrial solid waste BFS, which possesses a complex chemical composition. The HCPCMs were synthesized through a three-step process involving static melting, solid waste modification, and mixing–cold pressing–sintering. Then, the influence of the modification method and the amount of SiC thermal conductivity reinforced material on chemical compatibility and thermodynamic performance was explored. The results demonstrate that the predominant phase of the modified solid waste is Ca2Al2SiO7, which exhibits excellent chemical compatibility with chlorine salt. HCPCMs containing less than 50 wt.% chloride content exhibit good morphological stability without any cracks, with a melting temperature of 661.76 °C and an enthalpy value of 108.73 J/g. Even after undergoing 60 thermal cycles, they maintain good chemical compatibility, with leakage rates for melting and solidification enthalpies being only 6.3% and 0.23%, respectively. The equilibrium was achieved when 40 wt.% of chloride salt was encapsulated upon the addition of 10% of SiC, and the incorporation of SiC resulted in an enhancement of thermal conductivity for HCPCMs to 2.959 W/(m·K) at room temperature and 2.400 W/(m·K) at 200 °C, with an average increase of about 2 times. The cost of the prepared HCPCMs experienced a significant reduction of 81.3%, demonstrating favorable economic performance and promising prospects for application. The research findings presented in this article can offer significant insights into the efficient utilization of solid waste.

Computational thermodynamics‐assisted design of nitrate‐based phase change materials for waste heat recovery

Transient Performance of a Thermal Energy Storage-Based Heat Sink Using a Liquid Metal As the Phase Change Material

Investigation on the Melting Performance of a Phase Change Material Based on a Shell-and-Tube Thermal Energy Storage Unit with a Rectangular Fin Configuration

Preparation and characterizations of a novel temperature-tuned phase change material based on sodium acetate trihydrate for improved performance of heat pump systems

The Effects of Nucleating Agents on Phase Transition of a Salt Hydrate Phase-Change Material for Thermal Energy Storage Heat Exchangers

Charge Assessment for Nitrate-Based Salt as a Phase Change Material for a Medium-Temperature Latent Storage Tank

Experimental Analysis of Salt Hydrate Latent Heat Thermal Energy Storage System With Porous Aluminum Fabric and Salt Hydrate as Phase Change Material With Enhanced Stability and Supercooling

Characterisation of Promising Phase Change Materials for High Temperature Thermal Energy Storage

Calcium chloride hexahydrate based supercooling phase change material for a long-term recovery of low-grade thermal energy

Research on NaCl-KCl High-Temperature Thermal Storage Composite Phase Change Material Based on Modified Blast Furnace Slag

The Thermal Stratification Evaluation of Phase-Change Materials in a Heat Storage Tank: Computational Fluid Dynamics and Experimental Study

Experimental and Numerical Analysis for the Discharge Performance of a High Temperature Phase Change Material with Low-Cost Wire Mesh

Experimental evaluation of binary and ternary eutectic phase change material for sustainable thermal energy storage

Development and Investigation of Nitrate Phase Change Filler Material for Solar Process Heating Applications

Constructing heat conduction path and flexible support skeleton for PEG-based phase change composites through salt template method

Study on the preparation and thermal properties of binary mixed chloride salts

Thermal performance characterization of a thermal energy storage tank with various phase change materials

Incorporated Surfaces and Confined Spaces of Na2HPO4·12H2O–Layered Vermiculite Nanosheets for Phase Change Materials with Enhanced Thermal Properties

Research on the low-temperature waste heat storage performance of a novel microencapsulated phase change material with a double-shell encapsulation of hexadecylamine

Thermal Performance of Industrial-Grade CH3COONa·3H2O-based Composite Phase Change Materials in a Plate Heat Storage Unit

Development and thermal properties of a novel sodium acetate trihydrate-Acetamide-micron/nano aluminum nitride composite phase change material