Abstract:Metal oxide nanomaterials directly grown on conductive substrates are optimal electrode materials because their structures allow for rapid ion and electron transport and thereby reduce internal resistance in the electrode. The development of such binder-free, self-supporting electrodes is of great significance for applications in electrocatalysis. In this work, a simple hydrothermal in situ self-assembly reaction and annealing process was developed to prepare three kinds of nickel oxide @ carbon felt (NiO@CF) nanocomposites with different morphologies. The influence of different precipitators (strong or weak bases) on the morphology of the resulting nano-sized nickel oxide nanocomposites was investigated. The microstructures of the NiO@CF samples were characterized with field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). When ammonia was used as the precipitator, NiO grew vertically on the surface of the carbon felt and formed a mesoporous nanosheet-like structure (NiO NSs@CF). As an electrocatalytic nitrogen reduction reaction (e-NRR) electrode, the NiO NSs@CF sample showed an excellent NH3 yield (71.3 μg h-1 mg-1 cat. ) and Faradaic efficiency (17.9 % at -0.5 V vs. RHE) in 0.1 M Na2 SO4 . The good performance was attributed to the vertical interleaved mesoporous sheet-like structure (with the pore size of 15 nm and the thickness of ∼30 nm) and the relatively high concentration of oxygen vacancies. First-principles calculations with strong on-site Coulomb interactions demonstrated that the presence of oxygen vacancy on NiO sample leads to a significantly stronger N binding over the surface, benefiting for the nitrogen gas adsorption and reduction. The e-NRR performance of this binder-free, flexible electrode material is superior to that of other reported nickel-based nanomaterials. This study highlights the potential of such binder-free carbon felt electrodes for use in e-NRR that could meet the needs of industrial production.

In Situ Growth of Fe 2 O 3 Nanorod Arrays on Carbon Cloth with Rapid Charge Transfer for Efficient Nitrate Electroreduction to Ammonia

In Situ Growth of Nitrogen-Doped Carbon-Coated γ-Fe<sub>2</sub>O<sub>3</sub> Nanoparticles on Carbon Fabric for Electrochemical N<sub>2</sub> Fixation

In Situ Growth Of Nitrogen-Doped Carbon-Coated Gamma-Fe2o3 Nanoparticles On Carbon Fabric For Electrochemical N-2 Fixation

A 3D FeOOH nanotube array: an efficient catalyst for ammonia electrosynthesis by nitrite reduction

Understanding first electron transfer kinetic process of electrochemical nitrate reduction to ammonia on Fe2O3 nanorods array

Boosting Electrochemical Nitrate Reduction to Ammonia by Fe Doped CuO/Co3O4 Nanosheet/Nanowire Heterostructures

Cu/NiO nanorods for efficiently promoting the electrochemical nitrate reduction to ammonia

High-Performance Electrochemical Nitrate Reduction to Ammonia under Ambient Conditions Using a FeOOH Nanorod Catalyst

Boosting electrochemical nitrate-to-ammonia conversion by self-supported MnCo2O4 nanowire array

Fe and Cu Double-Doped Co 3 O 4 Nanorod with Abundant Oxygen Vacancies: A High-Rate Electrocatalyst for Tandem Electroreduction of Nitrate to Ammonia

Heterostructure engineered construction of N-doped CuO@Co3O4 for highly efficient electrocatalytic reduction of nitrate to ammonia

Electrochemical ammonia synthesis via nitrate reduction on Fe single atom catalyst

Porous Two-dimensional Iron-Cyano Nanosheets for High-rate Electrochemical Nitrate Reduction

Oxygen vacancy-regulated nanorod array electrodes for boosting the electrocatalytic synthesis of ammonia from nitrate wastewater

A FeCo 2 O 4 nanowire array enabled electrochemical nitrate conversion to ammonia

A Simple Synthesis Of Co3o4@Cnt To Boost Electrochemical Nitrogen Fixation

Direct In Situ Vertical Growth of Interlaced Mesoporous NiO Nanosheets on Carbon Felt for Electrocatalytic Ammonia Synthesis

Nano-Polycrystalline Cu Layer Interlaced with Ti3+-Self-Doped TiO2 Nanotube Arrays as an Electrocatalyst for Reduction of Nitrate to Ammonia

High-Efficiency Electrosynthesis of Ammonia with Selective Reduction of Nitrate in Neutral Media Enabled by Self-Supported Mn 2 CoO 4 Nanoarray

N-doped Carbon–iron Heterointerfaces for Boosted Electrocatalytic Active and Selective Ammonia Production

Cascade Electrocatalytic Nitrate Reduction Reaching 100% Nitrate-N to Ammonia-N Conversion over Cu 2 O@CoO Yolk-Shell Nanocubes