Abstract:In this paper, the effect of thermomechanical treatment process on the hardening behavior, grain microstructure, precipitated phase, and tensile mechanical properties of the new high-strength and high-ductility Al-10.0Zn-3.0Mg-2.8Cu alloy was studied, and the optimal thermomechanical treatment process was established. The strengthening and toughening mechanisms were revealed, which provided technical and theoretical guidance for the engineering application of this kind of high strength-ductility aluminum alloy. Al-10.0Zn-3.0Mg-2.8Cu alloy cylindrical parts with external longitudinal reinforcement were prepared by a composite extrusion deformation process (reciprocal upsetting + counter-extrusion) with a true strain up to 2.56, and the organizational evolution of the alloys during the extrusion deformation process and the influence of pre-stretching treatments on the subsequent aging precipitation behaviors and mechanical properties were investigated. The results show that firstly, the large plastic deformation promotes the fragmentation of coarse insoluble phases and the occurrence of dynamic recrystallization, which results in the elongation of the grains along the extrusion direction, and the volume fraction of recrystallization reaches 42.4%. Secondly, the kinetic study showed that the decrease in the activation energy of precipitation increased the nucleation sites, which further promoted the diffuse distribution of the second phase in the alloy and a higher number of nucleation sites, while limiting the coarsening of the precipitated phase. When the amount of pre-deformation was increased from 0% to 2%, the size of the matrix precipitated phase decreased from 5.11 μm to 4.1 μm, and when the amount of pre-deformation was increased from 2% to 7%, the coarsening of the matrix precipitated phase took place, and the size of the phase increased from 4.1 μm to 7.24 μm. The finalized heat treatment process for the deformation of the aluminum alloy tailframe was as follows: solution (475 °C/3 h) + 2% pre-stretching + aging (120 °C/24 h), at which the comprehensive performance of the alloy was optimized, with a tensile strength of 634.2 MPa, a yield strength of 571.0 MPa, and an elongation of 15.2%. The alloy was strengthened by both precipitation strengthening and dislocation strengthening. After 2% pre-stretching, the fracture surface starts to be dominated by dense tough nest structure, and most of them are small tough nests, and small and dense tough nests are the main reason for the increase in alloy toughness after 2% pre-stretching deformation.

Influence of strain rates and aging time on microstructure and hardness of integrally compressed 6082 aluminum alloy

Effect of Aging Treatment on Microstructure and Mechanical Properties of As-Extruded AA6063 Aluminum Alloy

Comprehensive study of hot compression behaviors and microstructure evolution of solutionized 6082 aluminum alloy extruded bar

EFFECTS OF DEFORMATION ON THE MICROSTRUCTURE AND PROPERTIES OF 6082 ALUMINUM ALLOY

Effect of ageing treatment process on the microstructure development and mechanical properties of 6082 Al alloy

Effects of Aging Treatments on the Age Hardening Behavior and Microstructures in an Al-Mg-Si-Cu Alloy

Microstructure and mechanical properties of 6082 aluminum alloy processed by preaging and hot forging

Microstructural Influences Caused by Different Aging Strategies on the Strain-Dependent Damping of the High-Strength Aluminum Alloy AA7075

Effects of different initial states on dynamic tensile properties and microstructure of 7075 aluminum alloy

Effect of Aging Process on Strengthening Phase Particles of 6056 Aluminum Alloy for Bolts

Microstructures and Mechanical Properties of Al-Zn-Mg-Cu Alloys under Multi-Directional Severe Strain and Aging

EFFECT OF PRE-DEFORMATION ON AGE- HARDENING AND MICROSTRUCTURE IN Al-Mg-Si-Cu ALLOY

Influence of aging on microstructure, mechanical properties and stress corrosion cracking of 7136 aluminum alloy

Microstructural evolutions and mechanical properties of 6082 aluminum alloy part produced by a solution-forging integrated process

Effect of Multidirectional Forging on the Microstructures and Mechanical Properties of the Al–Mg–Si Alloy

The Influence of Creep Ageing on the Hardening Behavior and Microstructure of 7050 Aluminum Alloy

Effects of aging temperature on microstructure and high cycle fatigue performance of 7075 aluminum alloy

Study on the Aging Precipitation Behavior and Kinetics of Al-10.0Zn-3.0Mg-2.8Cu Alloy by Pre-Deformation Treatment

Investigation of Pre-Aged Hardening Single-Point Incremental Forming Process and Mechanical Properties of AA6061 Aluminum Alloy

Microstructure and mechanical properties of Al-Mg-Si alloy during solution heat treatment and forging integrated forming process

Influence of different rolling processes on the microstructures and mechanical properties of 6016 aluminum alloy