Abstract:A continuum damage mechanics (CDM) failure model, which can predict both the initiation and propagation of cracks in brittle materials such as ceramics and nuclear graphite, has been developed and implemented into the commercial finite element code ABAQUS. In this model, both the stress-based failure criterion and fracture-mechanics-based failure criterion are used to define the damage surface, and a softening parameter 'n' is adopted to control the rate of damage development. Specifically, a change in the softening parameter changes the shrinkage rate of the damage surface, thus giving rise to different traction-displacement behaviors at the interface where crack initiation and propagation are taking place. This paper studies the effect of the degree of softening in the CDM model on the predicted strength of brittle materials subjected to loadings with different stress gradients. 0. FOREWORD The failure of brittle materials, such as nuclear graphite and ceramics, is not only a function of component geometry and size but also of loading mode. Therefore, full-size component testing is often required to determine the failure loads. Although various computational methods have been developed to predict the lifetime and failure load of brittle components, the absence of a satisfactory failure model is still an impediment to accurate failure predictions. Several commonly used failure models of graphite were reviewed in Ref. (1). The authors showed that simple models based on critical stress, critical strain and critical strain energy density criteria were remarkably unsuccessful in describing the experimental results. A continuum damage mechanics (CDM) model (2) has been developed for nuclear graphite at the Manchester School of Engineering (MSE), University of Manchester. The CDM model can be viewed as an extension or generalization of the cohesive zone model (3), in that it couples together the effects of mode-I and mode-II loadings. An interface with no thickness is introduced into the continuum solid at positions where potential crack surfaces may form. Within the interfacial constitutive law, which relates tractions and displacements across the interface, a damage parameter is introduced to take account of the effects of damage such as mcro-cracking. A damage surface is then constructed using both the conventional stress-based and fracture-mechanics-based failure criteria. Therefore, the CDM model can predict both the initiation and propagation of cracks in components with high stress concentration or even stress singularity.

On the modelling and simulation of a nuclear graphite brick: effects of cracks and interactions

Large Scale Modelling of Damage and Failure of Nuclear Graphite Moderated Reactor

Effects of Nuclear Graphite Material Properties Changes on Advanced Gas Cooled Reactor Bricks Contact Conditions and Ovality

A mathematical stress analysis model for isotropic nuclear graphite under irradiation condition

Predicting and visualizing crack propagation in nuclear graphite

Earthquake response of a multiblock nuclear reactor graphite core: Experimental model vs simulations

A Nonlocal Meso-Scale Damage Model for Nuclear Graphite

Simulation of crack propagation behavior of nuclear graphite by using XFEM, VCCT and CZM methods

Monte Carlo Simulation of In-Situ Multi-Scale Damage Detection of AGR Graphite

An investigation of fracture behaviors of NBG-18 nuclear graphite using in situ mechanical testing coupled with micro-CT

Numerical Simulation Of Graphite Properties Using X-Ray Tomography And Fast Multipole Boundary Element Method

THE EFFECT OF SOFTENING ON THE PREDICTED STRENGTH OF BRITTLE MATERIALS USING A CONTINUUM DAMAGE MECHANICS FAILURE MODEL

Experiment Study On Collision Of Graphite Dowel-Brick Structures

Dimensional change, irradiation creep and thermal/mechanical property changes in nuclear graphite

Radiation damage study on graphite from multiple cascade events in molecular dynamics simulation

Experimental and Simulation Study on Stress Concentration of Graphite Components in Tension

Effects of Tensile and Compressive Stresses on Damage Evolution Law of Nuclear Graphite

The Stress and Reliability Analysis of Htr'S Graphite Component

Effect Of Irradiation Deformation And Graphite Varieties On The Irradiation Equivalent Stress And Life Of Nuclear Graphite

Study on Failure Mechanism of Line Contact Structures of Nuclear Graphite

Static and Dynamic Fracture Toughness of Graphite Materials with Varying Grain Sizes