Reaction kinetics of chitosan nanogels crosslinked by genipin

Xinyue Zhao,Jian Tang,Yanhua Liu,Bing Hu,Quan Chen,Yonggang Liu

DOI: https://doi.org/10.1016/j.chroma.2023.464427

IF: 4.601

2023-10-05

Journal of Chromatography A

Abstract:Crosslinking of chitosan chains in dilute solution by natural crosslinker genipin leads to biocompatible nanogels. Here we investigated the reaction kinetics between chitosan and genipin in a 200 mM acetate buffer at 37 °C, and the structural and conformational evolutions of the nanogels during the crosslinking reaction by multi detection asymmetric flow field-flow fractionation (AF4). Upon crosslinking by genipin, the z-average hydrodynamic radius R hz of the chitosan chains increased from 26 nm to 130 nm, while the weight average molar mass M w increased from 2.0 × 10 5 g/mol to 1.8 × 10 7 g/mol. The crosslinking reaction appeared to be first-order and size-dependent. In particular, the intrachain crosslinking reaction was preferentially for nanogels having the larger size, leading to formation of branched chains/nanogels having a wide range of molar masses between 10 6 and 10 8 g/mol but a similar radius of gyration R g ∼ 40 nm. For the largest nanogel fractions with M > 2.0 × 10 8 g/mol, both R g and R h showed a scaling relation with exponent 1/3 and a structure parameter R g / R h = 0.74, as expected for the hard sphere particle. The reaction was accompanied by a reduction of charge density and an increase in hydrophobicity of chitosan nanogels, which plays a key role in the formation of uniform size nanogels with chain density r ( R h ) up to 0.45 g/cm 3 .

chemistry, analytical,biochemical research methods