Abstract:A lignin modified salt-resistant branched high-performance water reducer was prepared via free radical polymerization. The water-reducing agent was identified through its NMR spectrum, elemental analysis, Fourier transform infrared analysis, thermal gravimetric analysis, and scanning electron microscopy. The experiment conducted on cement paste demonstrates that the water-reducing efficiency can reach a maximum of 44%. Additionally, the significant spatial steric hindrance of the application enhances the dispersal capability of the water-reducing agent, resulting in effective water reduction and reduced viscosity. In addition, its compressive strength is the highest after 3-day curing and 3-, 7-, 28-day standard curing, and it has the best overall performance both in water and saline water prepared systems. The application in oil cement slurry shows that it exhibits a good dispersibility in fresh water, saline water, and substitute ocean water. In the Halfaya and Missan Oilfields of Iraq, BHPWR was used in a slurry with a density of 2.28 g/cm3 for casing the salt paste layer of five wells. The cementing results exceeded expectations with 100% qualified including over 85% excellent.

What problem does this paper attempt to address?

The paper primarily addresses the issue of reduced efficiency of water reducers when preparing concrete in high-salinity environments. Specifically, the research team developed a novel salt-resistant branched high-performance water reducer (BHPWR) to improve the fluidity and dispersibility of concrete slurry prepared in seawater, brine, or alkaline water. ### Research Objectives 1. **Develop a novel water reducer**: Prepare a salt-resistant branched high-performance water reducer based on lignin modification through radical polymerization. 2. **Improve concrete fluidity**: Enhance the fluidity and dispersibility of concrete slurry in saline environments. 3. **Enhance concrete performance**: Ensure that concrete prepared in both fresh water and saline water has high compressive strength and other excellent properties. ### Main Contributions - **Synthesis and Characterization**: The newly synthesized water reducer was characterized in detail using nuclear magnetic resonance spectroscopy (NMR), Fourier-transform infrared spectroscopy (FTIR), elemental analysis, thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). - **Performance Testing**: Experimental results showed that the water reduction rates of BHPWR-3 in fresh water and saline water could reach 45% and 44%, respectively. It effectively improved the fluidity of concrete, achieving a slump of 500 mm, and exhibited the highest compressive strength after 3 days of curing. - **Practical Application**: BHPWR-3 was applied to cement slurry with a density of 2.28 g/cm³ for cementing salt gypsum layers in the Halfaya and Missan oil fields in Iraq. The measured results exceeded expectations, with a qualification rate of 100% and an excellent rate of over 85%. In summary, this study successfully developed a novel salt-resistant branched high-performance water reducer, which not only improved the fluidity and dispersibility of concrete in saline environments but also ensured its excellent mechanical properties.

The Synthesis and Performance of a Novel Lignin Modified Salt-Resistant Branched High-Performance Water Reducer

Preparation of Lignosulfonate Water Reducer from Wheat Straw Alkali Lignin

Study on Performance of Compound-modification Sulfonated Wheat Straw Lignin GSL As Water Reducer

Environmentally friendly and salt-responsive polymer brush based on lignin nanoparticle as fluid-loss additive in water-based drilling fluids

Synthesis and Performance of A Self Crosslinkable Acrylate Copolymer with High Compatibility for an Oil Well Cement Modifier

On Concrete Water Reducing Agent from Modified Lignosulfonate

Synthesis and Characterization of Polycarboxylate High Range Water-reducer

Study on Combination Use of Polycarboxylate Based Water Reducer and Lignosulphate Based Water Reducer

Synthesizing and Evaluation of Chemically Modified Straw Pulp Lignin Based Water Reducer

Study on Modification of Alkali Lignin and its Water-reducing and Disperse Properties

Synthesis of novel zwitterionic polymers and their properties as filtrate reducer for water‐based drilling fluid

Use of Water Reducer to Enhance the Mechanical and Durability Properties of Cement-Treated Soil

A zwitterionic copolymer as fluid loss reducer for water-based drilling fluids in high temperature and high salinity conditions

Laponite-polymer composite as a rheology modifier and filtration loss reducer for water-based drilling fluids at high temperature

Revitalizing biopolymers to prepare temperature-resistant and salt-tolerant filtrate reducer by combining light-driven lignin depolymerization and subsequent photopolymerization on MIL-100(Fe)-NH2(20) photocatalyst

Salt-Responsive Zwitterionic Polymer Brush Based on Modified Silica Nanoparticles as a Fluid-Loss Additive in Water-Based Drilling Fluids

Graft Sulfonation and Water Reducing-Performance Strengthening Effect of Acid Precipitation Lignin

Synthesis and Evaluation of a Water-Soluble Hyperbranched Polymer as Enhanced Oil Recovery Chemical

A high salt tolerance and low adsorption drag reducer based on non-covalent enhancement

A Novel and Highly Efficient Polymerization of Sulfomethylated Alkaline Lignins Via Alkyl Chain Cross-Linking Method

Nanolaponite/Comb Polymer Composite as a Rheological Modifier for Water-Based Drilling Fluids