Integrating N, P, Ni into 3D carbon felt anode for high-performance lithium metal batteries

Jinmin Cheng,Hongchao Sun,Ya Chen,Shifei Kang,Lifeng Cui

DOI: https://doi.org/10.1016/j.jallcom.2023.173366

IF: 6.2

2024-01-09

Journal of Alloys and Compounds

Abstract:Lithium metal batteries are widely regarded as one of the most promising battery technologies because of their low electrochemical reduction potential and the superior theoretical specific capacity of lithium metal. However, the dendrite issue must be addressed prior to the fabrication of stable rechargeable lithium batteries. Herein, a method involving the injection of molten lithium into three-dimensional (3D) carbon felt doped with nitrogen (N), phosphorus (P), and nickel (Ni) was employed to obtain high-performance lithium batteries. Experimental observations indicate that the co-doping of N, P, and Ni significantly improves the lithiophilicity of the carbon felt. This improvement not only enables uniform loading of molten lithium but also facilitates reversible stripping and deposition of lithium. The porous carbon felt provides space for anode volume expansion, effectively suppressing the growth of lithium dendrites. The modified 3D anode can be stably operated for over 600 h under a current density of 1 mA·cm −2 , showcasing impressive long-term stability. Moreover, the capacity retention rate remains at 82.5% after over 300 cycles. These findings elucidate the potential application prospects of meticulously-designed 3D-structured stable lithium metal anodes in the next-generation rechargeable lithium metal batteries.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering