Urea-assisted synthesis of nickel sulfide arrays with enriching high-valence W species to boost Ni 3+ active sites for water oxidation
Ruirui Zhang,Jingce Bi,Yi Wang,Ningning Liu,Zhiqiang Liang,Junbiao Wu,Zhuopeng Wang,Xia Zhang,Yide Han
DOI: https://doi.org/10.1016/j.apsusc.2023.158176
IF: 6.7
2023-08-11
Applied Surface Science
Abstract:Introduction of high-valence transition metal in nickel sulfides is an effective strategy to boost Ni 3+ active sites, resulting in excellent OER performance. However, it is a challenge to enhance the amount of high-valence transition metal for ensuring Ni 3+ -rich specie in nickel sulfides. In this work, one-pot urea-assisted synthesis method was applied to fabricate Ni 3+ -rich W,V co-modified nickel sulfide nanohorn arrays grown on nickel foam (W, V-NiS@NF-UR1) as OER electrocatalyst in alkaline media. Urea can not only improve the crystallinity of electrocatalysts but also regulate their composition, which is favorable for the formation of the high content of W 6+ species in the electrocatalyst, consequently increasing the Ni 3+ active sites and enhancing the electrocatalytic OER performance. As a result, a small overpotential of 214 mV is required for a current density of 10 mA cm −2 by the as-prepared W, V-NiS@NF-UR1 electrocatalyst and a small Tafel slope of 69 mV dec −1 is observed in 1 M KOH. Meanwhile, the introduction of V species is also beneficial to keeping the high-valence W 6+ in the electrocatalyst during the sulfurization process. For comparison, the counterpart electrocatalysts were also investigated systematically without urea.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films