Modification of Cu/ZrO2 Catalysts by Rare Earth Elements for Catalytic Hydrogenolysis of Glycerol to 1,2-Propanediol
FU Rui-feng,LI Huai-you,DUAN Wei-jie,JIANG Zhi-dong
DOI: https://doi.org/10.13550/j.jxhg.2015.05.011
2015-01-01
Abstract:A series of rare earth elements promoted Cu / Zr O2 catalysts were prepared by impregnation of incipient wetness method and tested in gas-phase hydrogenolysis of glycerol to 1,2-propanediol where the 40% glycerol aqueous solution was adopted as the feed. The pore structure,morphology,crystalline phase and reducibility of the catalysts were characterized by BET,TEM,XRD and H2-TPR,respectively. The typical reaction conditions of hydrogenolysis were selected as 220 ℃,1 MPa,molar ratio of hydrogen to glycerol 100,and liquid space velocity 0. 25 g-glycerol /( g-catalyst · h). Three kinds of supports,namely Si O2,Al2O3 and Zr O2 were screened in the preliminary tests,but all these unprompted catalysts deactivated quickly under the tested reaction conditions. The stability of Cu / Si O2 promoted by impregnation of Ce was substantially improved,but still lasted only for around 700 h. For purpose of modification,the elements of rare earths La,Ce,Y were added in Zr O2 by coprecipitation method. The performance of catalysts was obviously improved after doping of La,Ce and Y in Zr O2 support,among which,yttria stabilized Zr O2(YSZ) was the best in activity and selectivity. Then,Ce was introduced as a promoter by successive impregnation of Cu and Ce precursors. The best catalyst was found to be 18% Cu ~ 4% Ce O2/ YSZ,with the yield of 1,2-propanediol over 93%. Instrumental characterization revealed that this catalyst contained an open pore structure and BET specific surfacearea 107 m2/ g,while its Cu O crystal was also the smallest in size and easiest to reduce. Time-on-stream test was carried out with the thoroughly optimized catalyst,a 1,2-propanediol yield over 94% was maintained over 1600 h,foreseeing a prospect of industrial application.