Abstract:Cerium dioxide (CeO2) 2 ) supported palladium (Pd) catalysts have found widespread application in CO oxidation reaction owing to their exceptional catalytic performance. The morphology of the CeO2 2 support dictates the exposed crystal plane, exerting a profound influence on surface structure and redox properties. This is crucial as the atomic arrangement at the surface directly impacts catalytic activity. In this study, a range of CeO2 2 supports with diverse morphologies ( e.g. nano-octahedra, nano-cubes, nano-particles, nano-spheres, and nano-rods) were successfully synthesized through hydrothermal methods and subsequently supported with Pd for CO oxidation. The spherical 1Pd/CeO2-S 2 -S catalyst, revealing exposed (111) + (100) crystal planes, exhibited significantly higher CO catalytic oxidation activity compared to the catalysts with other morphological CeO2 2 supports. The results indicated a positive correlation between the content of Pd x Ce 1-x O 2-y species and catalytic activity. Notably, this species was most abundantly formed in the spherical 1Pd/CeO2-S 2 -S catalyst with exposed (111) + (100) crystal planes. The presence of this active species facilitated the formation of surface defects, increased oxygen vacancy concentration, and enhanced metal-support interaction, consequently greatly improving the CO low-temperature catalytic oxidation activity. Consequently, the oxidation state of Pd in the Pd/CeO2 2 catalyst could be effectively regulated by controlling the exposure of (111) + (100) crystalline surfaces of the CeO2 2 support, further optimizing the catalytic performance of the Pd/CeO2 2 catalytic system.

Suppressing catalyst deactivation on Pd/CeO2 for selective oxidation of glucose into gluconic acid

Pd/CeO2 Interface with Abundant Oxygen Vacancies for Alkaline Hydrogen Evolution/Oxidation Reaction

Noble-Metal-Free WO3-Decorated Carbon Nanotubes with Strong W–C Bonds for Boosting an Electrocatalytic Glucose Oxidation Reaction

Enhanced Low-Temperature CO Oxidation Activity Through Crystal Facet Engineering of Pd/CeO2 Catalysts

The Synthesis of Carbon Black-Loaded Pt Concave Nanocubes with High-Index Facets and Their Enhanced Electrocatalytic Properties toward Glucose Oxidation

Enhancing the Electrocatalytic Activity of Pt-Pd Catalysts by Introducing Porous Architectures

Cerium(III) phosphate as a promising support for gold catalysts addressed to selective oxidation of glucose under base-free conditions

Influence of the Method of Preparation of the Pd-Bi/Al2O3 Catalyst on Catalytic Properties in the Reaction of Liquid-Phase Oxidation of Glucose into Gluconic Acid

Insight into the roles of Pd state and CeO2 property in C3H8 catalytic oxidation on Pd/CeO2

Selective scission of glucose molecule by a Pd-modulated Co-based catalyst for efficient CO2 reduction under mild conditions

Single-atom platinum promotes Cu(I)/Cu(II) redox loop of Cu aerogels for efficient glucose electrooxidation

Promoting Effects of Pretreatment on Pd/CeO2 Catalysts for CO Oxidation

Enhanced Migration of Oxygen on Ag-Modified Pd/Ceo2 Catalyst

Boosting the Catalytic Performance of Al2O3-supported Pd Catalysts by Introducing CeO2 Promoters.

Enhanced high-temperature CO 2 electrolysis on CeO 2 by inducing under-coordinated dual-atom active sites

Revealing the Crystal Facet Effect of Ceria in Pd/CeO 2 Catalysts toward the Selective Oxidation of Benzyl Alcohol

NiCu-based catalysts with high selectivity for electro–oxidation of glucose to formic acid

Tuning the Product Selectivity Toward the High Yield of Glyceric Acid in Pt−CeO2/CNT Electrocatalyzed Oxidation of Glycerol

Revealing the Crystal Facet Effect of Ceria in Pd/CeO2 Catalysts Toward the Selective Oxidation of Benzyl Alcohol

Highly Active Oxidation Catalysts through Confining Pd Clusters on CeO2 Nano‐Islands

Selective oxidation of glycerol to dihydroxyacetone over N-doped porous carbon stabilized CuxO supported Au catalysts