Abstract:Materials with the perovskite structure are extensively studied because of exhibiting enormous properties and these materials have proven their importance in many ways of our daily life. In the present approach Na2MgSiZ6 (Z = I, Br, Cl) halides were extensively studied and it was realized that all these halides display semiconducting nature having indirect band gaps. The semiconducting nature of the Na2MgSiZ6 (Z = I, Br, Cl) halides were also confirmed from their TDOS results as well. The optimized values of the lattice constants acquired were: 11.70 Å, 10.4 Å, & 10.22 Å for the Na2MgSiI6, Na2MgSiBr6, & Na2MgSiCl6, respectively. Moreover, higher value of volume was observed for the Na2MgSiI6 compound; while smallest value was seen for the Na2MgSiCl6 compound. Na2MgSiCl6 compound elucidated brittle nature; however, Na2MgSiBr6 and Na2MgSiI6 were found to have ductile nature. All the three materials showed attractive values of optical conductivities, which make these investigated materials as befitting candidates for the solar cells, LEDs, detectors, and various other optoelectronic devices. From the negative values of formation energies for all the Na2MgSiZ6 (Z = I, Br, Cl) halides, it was comprehended that these compounds can be synthesized practically.

Enchanting optical, electronic, and mechanical properties of the sodium based Na2MgSiZ6 (Z = I, Br, Cl) halides have been explored through DFT.