Catalytic graphitization of coke carbon by iron: Understanding the evolution of carbon Structure, morphology and lattice fringes

Hongtao Li,Hang Zhang,Kejiang Li,Jianliang Zhang,Minmin Sun,Buxin Su

DOI: https://doi.org/10.1016/j.fuel.2020.118531

IF: 7.4

2020-11-01

Fuel

Abstract:<p>The catalytic graphitization process of coke carbon with iron was investigated in the temperature range of 1100 °C–1500 °C using X-ray diffraction, scanning electron microcopy, high-resolution transmission electron microscopy (HRTEM). The evolution of micro-crystal graphite lattice fringes was carefully analyzed by image processing of the HRTEM micrographs. A strong catalytic effect of iron on graphitization was observed at temperature above 1200 °C with an obvious increase of carbon structural orders. Iron was found to promote the decrease of d₀ ₀ ₂ value and increase of Lc values of the turbostratic carbon, while the d₀ ₀ ₂ value of the newly formed graphitic carbon is quite below that of the commercial graphite when it just forms at 1200 °C. The melting point of iron particles were decreased due to the significant carbon dissolution into iron, leading to the melting and aggregation of iron. The lattice fringe length and the stacking number of micro-crystal graphite were found to increase obviously, while no clear change of crystal orientation was observed. This indicates that the growth of micro-crystal graphite was along its original orientation. The carbon dissolution – graphite precipitation mechanism can be used to explain the catalytic graphitization process very well.</p>

energy & fuels,engineering, chemical

What problem does this paper attempt to address?

The paper aims to study the catalytic effect of iron on the graphitization process of coke and its mechanism. Specifically, the paper explores the impact of iron on the graphitization of two different types of coke (C1 and C4) through experiments conducted in the temperature range of 1100 to 1500 degrees Celsius. The main findings include:

1. **Catalytic Effect**: Above 1200 degrees Celsius, iron exhibits a strong catalytic effect, significantly promoting the ordering of the coke structure, lowering the initial temperature of graphitization, and enhancing the reduction of graphite interlayer spacing (d002 value) and the increase of crystallite size (Lc value).
2. **Microstructural Changes**: Observations through high-resolution transmission electron microscopy (HRTEM) revealed that during the catalytic graphitization process, the stripe length and stacking number of the graphite lattice significantly increased, but the crystal orientation did not show noticeable changes.
3. **Morphological Changes**: The surface of coke particles became smoother, with clearer edges and corners, resembling the morphology of graphite crystals. Iron particles began to melt and aggregate at 1200 degrees Celsius, indicating a substantial dissolution of carbon in iron, which led to a reduction in the melting point of iron.
4. **Mechanism Analysis**: The study suggests that the mechanism of iron-catalyzed graphitization is primarily a dissolution-precipitation mechanism. The specific steps include: solid iron particles attaching to the coke surface, iron particles melting and encapsulating the coke surface, interaction between iron and carbon leading to carbon dissolution and graphite precipitation, ultimately forming graphene layers.

Through these experimental results, the paper reveals the significant role of iron in the graphitization of coke and its detailed mechanism. This research not only helps in understanding the behavior of coke in industrial blast furnaces but also provides a theoretical basis for the graphitization of other carbon materials.