RETRACTED: Ultra-fast one-step synthesis and surface engineering of mesoporous 3D α- Fe2O3 hollow nanospheres for high-performance and stable negative electrode for supercapacitors

Muhammad Sufyan Javed,Abdul Jabbar Khan,Saima Batool,Muhammad Idrees,Muhammad Arshad,Tyyaba Najam,Zhongwu Liu,Wenjie Mai

DOI: https://doi.org/10.1016/j.apsusc.2020.146634

IF: 6.7

2020-10-01

Applied Surface Science

Abstract:<p>Supercapacitors (SCs) have received considerable attention in portable digital devices because of their long life span and high power densities. However, low energy densities of SCs limited their practical applications due to the lack of high-performance negative electrode materials. This work demonstrates the surface engineering of α-Fe₂O₃ hollow nanospheres (α-Fe₂O₃-HNS) by controlled crystal growth through hollowing mechanism by the Ostwald ripening approach using facile one-step and low-cost hydrothermal method. The formation of α-Fe₂O₃-HNS was confirmed by scanning and transmission electron microscopy and further characterized by a variety of analytical methods. To investigate the electrochemical properties of α-Fe₂O₃-HNS, we systemically tested it in aqueous electrolyte under the extended potential window of −1.2–0.0 V versus Ag/AgCl. Among three samples of α-Fe₂O₃ nanospheres, the α-Fe₂O₃-HNS sample manifests a record high specific capacitance of 1041.18 F g⁻¹ while partially hollow and solid α-Fe₂O₃ nanospheres displayed relatively low specific capacitances of 534.31 and 325.38 F g⁻¹ at 1 A g⁻¹, respectively. The α-Fe₂O₃-HNS sample demonstrates excellent cycling retention of 98.88% while other samples retained 94.23% and 88.25%, respectively after 10,000 cycles at a high current density of 15 A g⁻¹. The surface engineering of α-Fe₂O₃-HNS offers not only the high surface area but also allows a large number of electroactive sites at electrode/electrolyte contact. Furthermore, we investigated the quantification of capacitive and diffusion controlled stored charge for high performance charge storage kinetics of as-prepared electrodes, by employing power's law and impressively α-Fe₂O₃-HNS sample reveals high capacitive type charge storage of (85% at 10 mV/s). The obtainable results fully exhibit the unique advantage of a hollow structure to fabricate superior negative electrode materials for supercapacitors.</p>

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films