Abstract:Introduction Formaldehyde (HCHO) is one of the major pollutants for indoor air pollution, which becomes an incentive of a variety of diseases. It is recognized that catalytic oxidation technology is an effective way to eliminate the formaldehyde pollutants [1]. On the basis of present research, some of the catalysts based on precious metals could achieve complete catalytic oxidation of HCHO. However, with the price of precious metals continuing to increase, it is still a challenge for developing low cost catalysts. It was reported that Ag nanoparticles or supported Ag catalysts exhibited some remarkable ability in the catalytic oxidation reaction including HCHO oxidation [2-5]. Therefore, Ag should be a good choice for catalytic oxidation of HCHO. In this work, we developed serial CeO2 and Ag/CeO2 nanosphere catalysts. The results showed that the HCHO oxidation ability was significantly improved on Ag/CeO2 nanosphere catalysts compared to normal Ag/CeO2 particle catalysts. The serial CeO2 and Ag/CeO2 catalysts were also characterized in detail, and the possible reaction mechanism for HCHO oxidation on Ag/CeO2 nanosphere catalysts were proposed based on In-situ DRIFTS experiments. Materials and Methods The CeO2 nanospheres were synthesized by hydrothermal methods. Ag/CeO2 nanospheres were prepared that a certain amount of AgNO3 (AR) was added and dispersed in the mixed solution in the process of CeO2 nanosphere preparation. The obtained catalysts are denoted as Ag/CeO2-N and CeO2-N, respectively. Meanwhile, the CeO2 and Ag/CeO2 bulk particles were prepared for comparison, and denoted as CeO2-P and Ag/CeO2-P, respectively. The serial CeO2 and Ag/CeO2 catalysts were also characterized by BET, XRD, HRTEM, XPS, H2-TPR, O2-TPD, and Raman spectra. The possible reaction mechanism for HCHO oxidation on Ag/CeO2 nanosphere catalysts were proposed based on In-situ DRIFTS experiments. Results and Discussion Figure 1 shows that both of CeO2-N and Ag/CeO2-N products are the nanosphere shapes with average sizes around 80-100 nm (Figure 2a and 2b). Ag/CeO2-N crystallite size is estimated by the HRTEM results (Figure 2c), in which the Ag/CeO2-N nanospheres are comprised of many small particles with a crystallite size of 2-5 nm, and there are clear voids among the small particles. The corresponding elemental maps of Ag/CeO2-N nanospheres show that both Ce and Ag are well distributed throughout the individual Ag/CeO2 nanosphere crystal (Figure 2d). The d lattice spacing is 0.312 nm, while FFT results indicate that the Ag/CeO2 nanosphere crystals mainly exposure (111) planes of fluorite structure of CeO2 (Figure 2e). Figure 2 shows the catalytic activity of HCHO oxidation on different CeO2 and Ag/CeO2 catalysts. It can be seen that maximum HCHO conversion of the serial catalysts ranks in the sequence of Ag/CeO2-N > Ag/CeO2-P > CeO2-N > CeO2-P in the whole temperature range. The CeO2-N catalysts show relatively higher catalytic activity than CeO2-P. When the Ag nano particles are doped onto CeO2-N support, surprisingly high HCHO conversions are gotten and reach approximately 100% conversion at 110 C. Ag/CeO2 nanospheres have relatively higher specific reaction rate and TOF implying that they should be potential catalysts for HCHO oxidation.

Water pretreatment promoting the removal of indoor formaldehyde over nano-CeO2 at ambient temperature

Indoor light boosted formaldehyde abatement over electrostatic self-assembled graphitic carbon nitride/ceric oxide at ambient temperature

Catalytic Ozonation of Formaldehyde with an Oxygen-Vacancy-Rich MnOx/γ-Al2O3 Catalyst at Room Temperature

Insights into the Synergistic Effect of Fe and Ce in Fenton-like Reactions Catalyzed by Chitosan/feooh/ceo2 Microspheres

Ag/Ceo2 Nanospheres: Efficient Catalysts for Formaldehyde Oxidation

Research on the elimination of low-concentration formaldehyde by Ag loaded onto Mn/CeO 2 catalyst at room temperature†

Highly dispersed Fe-Ce mixed oxide catalysts confined in mesochannels toward low-temperature oxidation of formaldehyde

Boosting the catalytic performance of Pt/TiO2 catalysts in room-temperature formaldehyde elimination by incorporating CeO2 promoters

High Surface Area Au/CeO2 Catalysts for Low Temperature Formaldehyde Oxidation

Low Cost and Highly Dispersed Ce/Na-ZSM-5 Catalysts Close to Atomic Dispersion for Enhancing Formaldehyde Oxidation.

Fluorescent light enhanced graphitic carbon nitride/ceria with ultralow-content platinum catalyst for oxidative decomposition of formaldehyde at ambient temperature

Preparation of porous MnO2/CeO2 composite for the effective removal of formaldehyde from air

A robust, eco-friendly, and biodegradable cellulose nanofiber composite film for highly effective formaldehyde removal at room temperature

Construction of strongly-coupled CeO 2 /MnO 2 heterogeneous catalysts for highly-efficient removal of formaldehyde

MnOx–CeO2 Derived from Mn–Ce-MOFs with Highly Efficient Removal of Formaldehyde

Complete oxidation of formaldehyde on Ag / CeO 2 nanosphere catalysts

Efficient Photothermal Elimination of Formaldehyde under Visible Light at Room Temperature by a MnO x-Modified Multi-Porous Carbon Sphere

Functional graphitic carbon nitride/hydroxyapatite heterojunction for robust formaldehyde removal at ambient temperature

Efficient activation of Pd/CeO2 catalyst by non-thermal plasma for complete oxidation of indoor formaldehyde at room temperature

Efficient Removal Of Formaldehyde By Nanosized Gold On Well-Defined Ceo2 Nanorods At Room Temperature

Zn-doped MnCe catalyst designed and applied for indoor low concentration formaldehyde removal and simultaneous antibacterial