Vanadium Oxide Intercalated with Conductive Metal–Organic Frameworks with Dual Energy‐Storage Mechanism for High Capacity and High‐Rate Capability Zn Ion Storage
Jingdong Guo,Jiaxin Liu,Weibing Ma,Zhiyuan Sang,Lichang Yin,Xueqi Zhang,Hao Chen,Ji Liang,De'an Yang
DOI: https://doi.org/10.1002/adfm.202302659
IF: 19
2023-06-15
Advanced Functional Materials
Abstract:Conductive metal–organic frameworks (c‐MOFs) is successfully preintercalated into the interlayer of vanadium oxides, thus, simultaneously achieve the improvement of capacity, rate performance, and cycling durability. Theoretical calculation discloses the relationship among various active sites, electronic structures, and the resulted Zn‐storage performances. This study demonstrates a versatile strategy that combines multiple energy storage mechanisms to achieve higher electrochemical performance. Vanadium oxides (VOx) feature the potential for high‐capacity Zn2+ storage, which are often preintercalated with inert ions or lattice water for accelerating Zn2+ migration kinetics. The inertness of these preintercalated species for Zn2+ storage and their incapability for conducting electrons, however, compromise the capacity and rate capability of VOx. Herein, Ni‐BTA, a 1D conductive metal–organic framework (c‐MOF), is intercalated into the interlayer space of VOx by coordinating organic ligands with preinserted Ni2+. The intercalated Ni‐BTA improves the conductivity of VOx by π–d conjugation, facilitates Zn2+ migration by enlarging its interlayer spacing, and stabilizes the crystal structure of VOx as interlayer pillars, thus simultaneously enhancing the material's rate capability and cycling stability. Meanwhile, a dual reaction mechanism of Zn2+ storage, i.e., the redox of V5+/V3+ in VOx and the rearrangement of chemical bonds (CN/CN) in Ni‐BTA, collaboratively contributes to an enhanced capacity. Consequently, this Ni‐BTA‐intercalated VOx material exhibits a high Zn2+ storage capacity of 464.2 mAh g−1 at 0.2 A g−1 and an excellent rate capability of 272.5 mAh g−1 at 5 A g−1. This work provides a general strategy for integrating c‐MOFs with inorganic cathode materials to achieve high‐capacity and high‐rate performance.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology