Abstract:Fe/N/C catalysts, synthesized through the pyrolysis of Fe-doped metal-organic framework (MOF) precursors, have attracted extensive attention owing to their promising oxygen reduction reaction (ORR) catalytic activity in fuel cells and/or metal-air batteries. However, post-treatments (acid washing, second pyrolysis, and so on) are unavoidable to improve ORR catalytic activity and stability. The method for introducing Fe3+ sources (anhydrous FeCl3) into the MOF structure, in particular, is a critical step that can avoid time-consuming post-treatments and result in more exposed Fe-Nx active sites. Herein, three different Fe doping strategies were systematically investigated to explore their influence on the types of active sites formed and ORR performance. Fe-NC(Zn2+), synthesized by one-step pyrolysis of Fe doped ZIF-8 (Zn2+) precursor which was obtained by adding the anhydrous FeCl3 source into the Zn(NO3)2•6H2O/methanol solution before mixing, possessed the highest Fe-Nx active sites due to the high-efficiency substitution of Zn2+ ions with Fe3+ ions during ZIF-8 growth, the strong interaction between Fe3+ ions and N atoms of 2-Methylimidazole (2-MIm), and ZIF-8's micropore confinement effect. As a result, Fe-NC(Zn2+) presented high ORR activity in the entire pH range (pH = 1, 7, and 13). At pH = 13, Fe-NC(Zn2+) exhibited a half-wave potential (E1/2) of 0.95 V (vs. reversible hydrogen electrode), which was 70 mV higher than that of commercial Pt/C. More importantly, Fe-NC(Zn2+) showed superior ORR stability in neutral media without performance loss after 5,000 cycles. A record-high open-circuit voltage (1.9 V) was obtained when Fe-NC(Zn2+) was used as a cathodic catalyst in assembled Mg-air batteries in neutral media. The assembled liquid and all-solid Mg-air batteries with high performance indicated that Fe-NC(Zn2+) has enormous potential for use in flexible and wearable Mg-air batteries.

Cu dopant triggering remarkable enhancement in activity and durability of Fe-N-C electrocatalysts toward oxygen reduction

Bimetallic diatomic nanoclusters with longitudinal Fe-O-Fe units and latitudinal Cu-S-Fe-S-Cu units as efficient ORR active sites

Fe, Cu Bimetallic Precursor-Driven Quaternary Active Sites Boost Oxygen Reduction / Evolution Reaction Bifunctional Catalysts

Influence of different Fe doping strategies on modulating active sites and oxygen reduction reaction performance of Fe, N-doped carbonaceous catalysts

In-situ Coupling FeN Nanocrystals with Fe/Fe3C Nanoparticles to N-doped Carbon Nanosheets for Efficient Oxygen Electrocatalysis

3D N-doped ordered mesoporous carbon supported single-atom Fe-N-C catalysts with superior performance for oxygen reduction reaction and zinc-air battery

Dual single-atom sites coupled with graphene-encapsulated core–shell Fe–Cu nanoalloy for boosting the oxygen reduction reaction

An active site pre-anchoring and post-exposure strategy in Fe(CN)64-@PPy derived Fe/S/N-doped carbon electrocatalyst for high performance oxygen reduction reaction and zinc-air batteries

Highly active Fe centered FeM-N-doped carbon (M = Co/Ni/Mn): A general strategy for efficient oxygen conversion in Zn–air battery

ZIF-8-derived Fe/P/N-co-doped Carbon as Efficient Electrocatalysts for Oxygen Reduction Reaction and Zinc-air Batteries

A ferric citrate derived Fe-N-C electrocatalyst with stepwise pyrolysis for highly efficient oxygen reduction reaction

Enhancing ORR/OER active sites through lattice distortion of Fe-enriched FeNi3 intermetallic nanoparticles doped N-doped carbon for high-performance rechargeable Zn-air battery

Boosting Oxygen Reduction Catalysis with Hierarchically Porous Fe-Doped Carbon by Chemical Vapor Deposition in Zn–Air Batteries

Cu/Fe dual atoms catalysts derived from Cu-MOF for Zn-air batteries

P-doped Fe-N-C catalysts as advanced bifunctional electrocatalyst for ORR, OER and Zn-air batteries

Boost oxygen reduction reaction performance by tuning the active sites in Fe-N-P-C catalysts

Boosted electrocatalytic activity and durability of CuFe/NC by modulating the interfacial composition and electronic structure for efficient oxygen reduction reaction

Cu/CuOx@C Composite as a High-Efficiency Electrocatalyst for Oxygen Reduction Reactions

High‐Activity Fe3C as pH‐Universal Electrocatalyst for Boosting Oxygen Reduction Reaction and Zinc‐Air Battery

ZIF-derived Bifunctional Cu@Cu–N–C Composite Electrocatalysts Towards Efficient Electroreduction of Oxygen and Carbon Dioxide

Palladium Enhanced Iron Active Site – An Efficient Dual‐Atom Catalyst for Oxygen Electroreduction