Strong solvent coordination effect inducing gradient solid-electrolyte-interphase formation for highly efficient Mg plating/stripping
Yaoyao Du,Yanmin Chen,Shuangshuang Tan,Jinlong Chen,Xueting Huang,Lianmeng Cui,Juncai Long,Zhongting Wang,Xuhui Yao,Bo Shang,Guangsheng Huang,Xiaoyuan Zhou,Lingjie Li,Jinfeng Wang,Fusheng Pan
DOI: https://doi.org/10.1016/j.ensm.2023.102939
IF: 20.4
2023-08-27
Energy Storage Materials
Abstract:Developing simple Mg-salt electrolytes without chlorine-containing additives is vital for the technical viability of rechargeable magnesium batteries (RMBs). However, the formation of an ion-blocking passivation layer on Mg anode in these electrolytes severely hinders the reversible Mg plating/stripping. Here, we successfully designed a highly efficient and chlorine-free Mg(SO 3 CF 3 ) 2 /ether electrolyte by introducing 2-methoxyethylamine (MOEA) with a strongly nucleophilic amidogen (-NH 2 ) donor to competing solvation coordination. The preferred decomposition of MOEA in MOEA-coordinated Mg-ion complex generates organic N-containing species in the inner layer, thus forming the gradient organic-inorganic solid-electrolyte-interphase (SEI). This gradient SEI enables a fast interfacial Mg 2+ migration and uniform Mg plating/stripping at 5 mA cm −2 with 5 mAh cm −2 . The Mg(SO 3 CF 3 ) 2 /ether/MOEA electrolyte exhibits high oxidation stability (3.5 V vs . Mg/Mg 2+ ), high average Coulombic efficiency (99.3 %, 1000 cycles), excellent rate performance (low overpotentials of 75, 270 and 570 mV at 0.5, 3.0 and 7.5 mA cm −2 , respectively) and realizes a stable cycle life of Mg||Mo 6 S 8 coin cell (300 cycles at 1 C), when using 50 μm Mg anode. Importantly, the relationships between solvation configuration, SEI chemistry and battery performance were successfully built for guiding the design of simple Mg-salt electrolytes in RMBs.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology