Abstract:Abstract Additive manufacturing (AM) is a developing manufacturing technology, which provides excellent attributes compared to other manufacturing techniques. However, one of the critical challenges is the presence of defects that hinder the mechanical properties of the parts, particularly the fatigue life. Experimental understanding of fatigue is a cumbersome process. Therefore, numerical prediction based on specified conditions (such as porosity and applied load) can be an alternative to experimental analysis at the design stage of AM parts. In this study, elastic–plastic finite element analysis (FEA) is performed to obtain the stress distribution around pores, and their resultant effect on fatigue life for L-PBF (laser powder bed fusion) produced AlSi10Mg alloy samples. The stress field is calculated for both single and multiple pore models, where stress concentration is evaluated as a function of the pore’s location and its size. It is found that both pore location and size affect the stress field; however, location effects dominate over pore size. For the same remote applied stress level, the stress concentration around the pore increases with an increase in pore size, and the local maximum stress occurs near the pores that are closest to the surface. The current study also evaluates the relative effect of porosity fraction, average pore size, and location. It is found that the magnitude and sensitivity of stress concentration are hierarchically controlled by porosity location, pore size, and porosity density. A multi-scale finite element (FE) model is proposed based on inherent porosity data measured using Computed Tomography (CT) to predict overall fatigue life. The fatigue cycles are calculated using the rainflow counting algorithm in FE Safe using the stress–strain data obtained from the proposed FEA model. Using the proposed model, it is possible to generate S–N curves for any loading condition for a given porosity condition (porosity density and average pore size). The S–N curve results obtained from the FE model are compared to the experimental observations. The predicted fatigue life shows approximately 5% error with experimental results at high stress loading conditions. However, the proposed model overpredicts the fatigue life at low stress loading by almost 30%.

Modified electric fatigue model of macro fibre composite (MFC): Significant influence of porosity on the fatigue failure of ferroelectric materials

Viscoelastic Fracture Mechanics-Based Fatigue Life Model in Asphalt-Filler Composite System

Prediction of long-term fatigue life of CFRP composite hydrogen storage vessel based on micromechanics of failure

Fatigue failure mechanism analysis and life prediction of short fiber reinforced polymer composites under tension-tension loading

Real-time Evaluating Temperature-Dependent Interfacial Shear Strength of Thermoplastic Composites Based on Stress Impedance Effect of Magnetic Fibers

Fatigue Damage Analysis of Prefabricated Concrete Composite Beams Based on Metal Magnetic Memory Technique

Fatigue life prediction method of carbon fiber-reinforced composites

Quantifying Fatigue Damage in Reinforced Concrete Beams Through Piezomagnetic Effect: A Fatigue-Magnetomechanical Coupling Approach

A Novel Method for Characterizing the Fatigue Crack Propagation of Steel Via the Weak Magnetic Effect

Characterization and modeling of fatigue behavior of chopped glass fiber reinforced sheet molding compound (SMC) composite

Strength and stiffness degradation modeling and fatigue life prediction of composite materials based on a unified fatigue damage model

Magneto-mechanical coupling model of ferromagnetic materials under fatigue loading and its application in metal magnetic memory method

Mechanical behavior simulation of particulate-filled composite at meso-scale by numerical manifold method

Multiscale-based multiaxial fatigue model of short fiber reinforced polymer composites under high-cycle proportional loading

Fatigue-driven failure criterion for progressive damage modelling and fatigue life prediction of composite structures

Analysing the effect of defects on stress concentration and fatigue life of L-PBF AlSi10Mg alloy using finite element modelling

Damage-entropy model for fatigue life evaluation of off-axis unidirectional composites

Experimental and computational analysis of bending fatigue failure in chopped carbon fiber chip reinforced composites

Prediction of Fatigue Life of Polyetherimide/Carbon Fiber Particulate Composites at Various Maximum Stresses and Filler Contents

Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates

An investigation of Fatigue Behavior and Residual Strength Model of Steel-GFRP Composite Bar