In vivo biocompatibility and biodegradability of poly(lactic acid)/poly(ε-caprolactone) blend compatibilized with poly(ε-caprolactone-b-tetrahydrofuran) in Wistar rats
Gabriel Conde,Jlia Ribeiro Garcia de Carvalho,Paula do Patrocnio Dias,Henriette Gellert Moranza,Gabriel Luiz Montanhim,Juliana de Oliveira Ribeiro,Marcelo Aparecido Chinelatto,Paola Castro Moraes,Sebastio Roberto Taboga,Paulo Henrique Leal Bertolo,Michelli Incio Gonalves Funnicelli,Daniel Guariz Pinheiro,Guilherme de Camargo Ferraz,Júlia Ribeiro Garcia de Carvalho,Paula do Patrocínio Dias,Sebastião Roberto Taboga,Michelli Inácio Gonçalves Funnicelli
DOI: https://doi.org/10.1088/2057-1976/abeb5a
2021-03-15
Abstract:Abstract Poly(lactic acid) (PLA) and poly( ε -caprolactone) (PCL) are two important aliphatic esters known for their biodegradability and bioresorbability properties; the former is stiffer and brittle while the smaller modulus of the latter allows a suitable elongation. The new biomaterials being developed from the blend of these two polymers (PLA and PCL) is opportune due to the reducing interfacial tension between their immiscible phases. In a previous study, PLA/PCL immiscible blend when compatibilized with poly( ε -caprolactone- b -tetrahydrofuran) resulted in enhanced ductility and toughness no cytotoxic effect in vitro tests. There is little published data on the effect of poly( ε -caprolactone- b -tetrahydrofuran) on PLA and PCL biocompatibility and biodegradability in vivo tests. This study focuses on evaluating the behavioral response and polymer-tissue interaction of compatibilized PLA/PCL blend compared to neat PLA implanted via intraperitoneal (IP) and subcutaneous (SC) in male Wistar rats, distributed in four experimental groups: neat PLA, PLA/PCL blend, sham, and control at 2-, 8- and 24-weeks post-implantation (WPI). An open-field test was performed to appraise emotionality and spontaneous locomotor activity. Histopathological investigation using hematoxylin-eosin (H&E) and picrosirius-hematoxylin (PSH) was used to assess polymer-tissue interaction. Modifications in PLA and the PLA/PCL blend’s surface morphology were determined by scanning electron microscopy (SEM). PLA group defecated more often than PLA/PCL rats 2 and 8 WPI. Conjunctive capsule development around implants, cell adhesion, angiogenesis, and giant cells of a foreign body to the biomaterial was observed in light microscopy. Both groups displayed a fibrous reaction along with collagen deposition around the biomaterials. In the SEM, the images showed a higher degradation rate for the PLA/PCL blend in both implantation routes. The polymers implanted via IP exhibited a higher degradation rate compared to SC. These findings emphasize the biocompatibility of the PLA/PCL blend compatibilized with poly( ε -caprolactone- b -tetrahydrofuran), making this biopolymer an acceptable alternative in a variety of biomedical applications.