Size-dependent chemical and magnetic ordering in L10-FePt nanoparticles

Chuan-bing Rong, Daren Li, Vikas Nandwana, Narayan Poudyal, Yong Ding, Zhong Lin Wang, Hao Zeng, J Ping Liu

2006-11-17

Abstract:FePt nanoparticles have great application potential in advanced magnetic materials such as ultrahigh-density recording media and high-performance permanent magnets.[1–3] The key for applications is the very high uniaxial magnetocrystalline anisotropy of the L10-FePt phase, which is based on crystalline ordering of the face-centered tetragonal (fct) structure, described by the chemical-ordering parameter S.[4] Higher chemical ordering results in higher magnetocrystalline anisotropy. Unfortunately, as-synthesized FePt nanoparticles take a disordered face-centered cubic (fcc) structure that has low magnetocrystalline anisotropy. Heat-treatment is necessary to convert the fcc structure to the ordered fct structure. Several previous theoretical and experimental investigations have been reported on the size-dependent chemical ordering of FePt nanoparticles.[5–9] It has been observed that the degree of ordering decreases with decreasing particle size of the sputtered FePt nanoparticles.[5, 6] Theoretical simulation predicted that the ordering would not take place when the particle size is below a critical value.[8, 9] However, there have not been systematic experimental studies on quantitative size dependence of chemical ordering of FePt nanoparticles due to the lack of monodisperse L10-FePt nanoparticles with controllable sizes. There are also few studies reported to date on the quantitative particle size dependence of magnetic properties, including the Curie temperature, coercivity, and magnetization of the L10-FePt phase, although it has been well accepted that there is a size effect on the ferromagnetism of any low-dimensional magnets.[10, 11 …