A novel AlCrFeMoTi high-entropy alloy coating with a high corrosion-resistance in lead-bismuth eutectic alloy

Jian Yang,Ke Shi,Wei Zhang,Qingsong Chen,Zhien Ning,Changda Zhu,Jiali Liao,Yuanyou Yang,Ning Liu,Wei Zhang,Jijun Yang
DOI: https://doi.org/10.1016/j.corsci.2021.109524
IF: 7.72
2021-07-01
Corrosion Science
Abstract:The amorphous AlCrFeMoTi high entropy alloy (HEA) coating with near-equal molar ratio was successfully deposited on F/M substrate by magnetron sputtering method. The coating exhibits excellent corrosion resistance against LBE with much thinner oxides scale and lower consumption of coating compared with the uncoated F/M steel (about an order of magnitude). The AlCrFeMoTi HEA coating has great potential in LBE-cooled fast reactor application. However, the elemental aggregation and local oxidation occur in the coating, and corrosion products of Fe-oxides and voids appear at the interface between the coating and substrate when the corrosion temperature reaches 650 ℃.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
### Problems Addressed by the Paper The paper primarily explores the issue of corrosion in structural materials within Lead-Bismuth Eutectic (LBE) cooled fast neutron reactors. Specifically: 1. **Corrosion Phenomena**: - Lead-Bismuth Eutectic alloy is considered a potential coolant for fourth-generation LBE-cooled fast neutron breeder reactors, but reactor components suffer from severe oxidation corrosion, dissolution corrosion, erosion, and liquid metal embrittlement, leading to significant degradation of structural material performance. - Among these corrosion phenomena, dissolution and oxidation are the main subjects of study. 2. **Limitations of Existing Protection Methods**: - Currently, controlling oxygen concentration to form a stable oxide layer is a common protective strategy, but it is challenging to maintain the target oxygen level in complex heat transfer systems. - The oxide layer becomes unstable at high temperatures, and an excessively thick oxide layer can detach and clog pipelines, reducing heat transfer efficiency. - Under low oxygen concentration conditions, dissolution corrosion can cause alloy elements (such as Ni and Mn) to directly transfer into the liquid metal. 3. **Design and Application of High-Entropy Alloy Coatings**: - Researchers have designed and prepared a novel AlCrFeMoTi high-entropy alloy (HEA) coating, which was deposited on ferritic/martensitic (F/M) steel substrates using magnetron sputtering technology. - This coating exhibits excellent corrosion resistance in LBE environments, forming a thinner and less consumptive oxide layer, which is advantageous compared to uncoated F/M steel (by approximately one order of magnitude). - However, at a corrosion temperature of 650°C, the coating shows element aggregation, local oxidation, and the formation of Fe-oxides and voids at the interface. In summary, the paper aims to develop a corrosion-resistant coating material suitable for LBE-cooled fast neutron reactor applications. Through experimental studies, the microstructure, mechanical properties, and LBE corrosion behavior of this novel AlCrFeMoTi high-entropy alloy coating at different temperatures were investigated, with the goal of finding an effective protective method to prevent or mitigate corrosion of structural materials in extreme environments.