Abstract:In the development of water splitting, the sluggish electrocatalytic kinetics of the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) have restricted their energy conversion efficiencies. Along with the continuous rise in the prices of noble metals and transition metals (such as cobalt and nickel), constructing high-efficiency HER/OER catalysts based on low cost transition metals, such as iron and manganese, is becoming more meaningful in developing industrialized water splitting devices. In this paper, in the absence of a template or active agent, three-dimensional, hierarchically porous FexMny nanoparticles (NPs) were embedded and nitrogen-doped carbon materials (denoted as FexMny@NC; x:y, representing the molar ratio of Fe:Mn) were successfully prepared via pyrolysis of corresponding precursors containing different metallic salt components. Various morphological, structural, and chemical characterization analysis demonstrate that at an Fe:Mn molar ratio of 3:1, the optimal Fe3Mn1@NC material shows high graphitization degree, rich mesoporous structures, a large surface area, and abundant carbon defects/edges, which promote the uniform dispersion of pyridinic-N (pyridinic-N-metal), graphitic-N, carbon oxygen bonds (C–O), manganese oxide (MnO) nanocrystals, and Fe3C NPs-embedded, N-doped carbon sheet (Fe3) active sites. In alkaline conditions, the HER onset potentials (Eonset) and potentials recorded at 10 mA cm-2 (E10) of the optimal Fe3Mn1@NC are just 84.8 and 156 mV more negative than those of 20 wt% platinum carbon (Pt/C). Meanwhile, the OER Eonset and E10 values of the optimal Fe3Mn1@NC are just 8 and 18.7 mV more positive than those of RuO2. Furthermore, optimized Fe3Mn1@NC catalysts were assembled into a water splitting cell, where the catalytic current density achieves 10 mA cm-2 at a low voltage of 1.6287 V (with superior catalytic stability), which is just 24.9 mV higher than that of the (-) 20 wt% Pt/C||RuO2 (+) benchmark (1.6038 V) under the same conditions. This work describes the regulating efficiency of Mn toward growing mesopores and opens new possibilities for the development of novel carbonaceous catalysts with excellent hydroxide catalytic efficiencies based on low cost Mn/Fe elements.

Hierarchical Fe–Mn binary metal oxide core–shell nano-polyhedron as a bifunctional electrocatalyst for efficient water splitting

Hierarchical Cu@CoFe Layered Double Hydroxide Core-Shell Nanoarchitectures As Bifunctional Electrocatalysts for Efficient Overall Water Splitting

Hierarchical core-shell structural Ni2P/NiMoO4 @CoP/FeP2 nanorods as difunctional electrocatalysts for efficient overall water splitting

Constructing hierarchical arrays with core–shell metal oxides@metal coordination polymers for efficient and stable overall water splitting

Construction of hierarchical FeNi3@(Fe,Ni)S2 core-shell heterojunctions for advanced oxygen evolution

Phosphorylated Co(OH)2@NiFe-LDH core–shell heterostructure for highly efficient alkaline water splitting

Hierarchical core–shell heterostructure FeMoS@CoFe LDH for multifunctional green applications boosting large current density water splitting

Hierarchical 2D Yarn-Ball Like Metal–organic Framework NiFe(dobpdc) As Bifunctional Electrocatalyst for Efficient Overall Electrocatalytic Water Splitting

Three-dimensional heterostructured MnNiCoP/FeOOH cross-linked nano-flake supported by Ni Foam as a bifunctional electrocatalysts for overall water splitting

Hierarchically Heterostructured Metal Hydr(oxy)oxides for Efficient Overall Water Splitting

Heterogeneous bimetallic Ni(OH) 2 -NiMoO 4 /NF as an efficient HER electrocatalyst for alkaline water splitting

FeNi3-Fe3O4 heterogeneous nanoparticles anchored on 2D MOF nanosheets/1D CNTs matrix as highly efficient bifunctional electrocatalyst for water splitting

Morphological modulation of iron carbide embedded nitrogen-doped hierarchically porous carbon by manganese doping as highly efficient bifunctional electrocatalysts for overall water splitting

MOF-derived Mn doped porous CoP nanosheets as efficient and stable bifunctional electrocatalysts for water splitting.

Hierarchical Cu Nanoarray/NiFe Hydroxide Nanostructures for Efficient Electrochemical Water Oxidation

Electroless Plating-Acid Etching Strategy to Synthesize Co–Fe–Mn–P Nanosheet Arrays Bifunctional Catalyst for Efficient Water Splitting

Design and Construction of 3D Porous Hierarchical Structure Ni–Fe–Co Bifunctional Catalyst Toward Highly Efficient Overall Water Splitting

In situ self-reconstructed hierarchical bimetallic oxyhydroxide nanosheets of metallic sulfides for high-efficiency electrochemical water splitting

Hierarchical Mesoporous NiO/MnO 2 @PANI Core-Shell Microspheres, Highly Efficient and Stable Bifunctional Electrocatalysts for Oxygen Evolution and Reduction Reactions.

Chemical Transformation Induced Core–Shell Ni2P@Fe2P Heterostructures toward Efficient Electrocatalytic Oxygen Evolution